Modified biopolymers and methods of producing and using the sam

ABSTRACT

Modified biopolymers, such as, charge-modified biopolymers, cross-linked biopolymers, and cross-linked, charged modified biopolymers are provided along with methods of producing and using the same.

RELATED APPLICATION DATA

This application claims the benefit of U.S. Provisional Patent Application Ser. No. 62/006,317, filed Jun. 2, 2014, the disclosure of which is incorporated herein by reference in its entirety.

FIELD

The present invention relates to modified biopolymers, including charge-modified biopolymers, cross-linked biopolymers, and cross-linked, charge-modified biopolymers. Methods of producing and using a modified biopolymer of the present invention are also provided.

BACKGROUND

Biopolymers are of interest due to their many uses. For example, biopolymers may be useful as absorbents, such as in diapers, hygiene products, and wound dressings, and may be useful as adsorbents. In addition, biopolymers may have the advantage of providing environmentally friendly products.

However, methods of forming and/or processing biopolymers into useful products, such as traditional heterogeneous wet chemistry methods, can often be complex, expensive, and inefficient.

The present invention addresses previous shortcomings in the art by providing modified biopolymers and methods of producing and using the same.

SUMMARY

A first aspect of the present invention includes a method for producing a cross-linked, charge-modified biopolymer comprising: combining a biopolymer and at least one charge-modifying agent to form a homogenous reaction blend; reacting the biopolymer and the at least one charge-modifying agent in the homogenous reaction blend; and cross-linking the biopolymer in the homogeneous reaction blend to form a cross-linked, charge-modified biopolymer.

The method may include reacting the biopolymer and the at least one charge-modifying agent to form a charge-modified biopolymer. In some embodiments, the charge-modified biopolymer may be cross-linked with a different biopolymer, which may optionally be charged-modified.

The method may include forming a homogenous reaction blend in an extruder, optionally using a reactive extrusion process.

Another aspect of the present invention includes a method for producing a cross-linked, charge-modified starch-chitosan comprising: combining starch, chitosan, at least one charge-modifying agent, a catalyst, and a plasticizer to form a homogenous reaction blend; charge-modifying the starch and chitosan to form a charge-modified starch and a charge-modified chitosan; and cross-linking the charge-modified starch and charge-modified chitosan to form a cross-linked, charge-modified starch-chitosan.

In a further aspect of the present invention, a method for producing a cross-linked, charge-modified starch-chitosan comprises: combining starch, a first charge-modifying agent, and a catalyst to form a homogeneous reaction blend comprising a charge-modified starch; adding charge-modified chitosan and a plasticizer to the homogeneous reaction blend comprising the charge-modified starch; and cross-linking the charge-modified starch and charge-modified chitosan to form a cross-linked, charge-modified starch-chitosan.

Another aspect of the present invention includes a method for producing a cross-linked, charge-modified starch-chitosan comprising: combining starch, a first charge-modifying agent, and a catalyst, to form a charge-modified starch; forming a homogeneous reaction blend comprising the charged-modified starch, a charged-modified chitosan, and a plasticizer; and cross-linking the charge-modified starch and charged-modified chitosan to form a cross-linked, charge-modified starch-chitosan.

A further aspect of the present invention includes a cross-linked, charge-modified biopolymer prepared according to a method of the present invention.

Another aspect of the present invention includes a cross-linked, charge-modified biopolymer having a charge density of at least 3 meq/g as determined by titration.

A further aspect of the present invention includes a cross-linked, charge-modified biopolymer having an increased charge density and/or degree of cross-linking compared to a cross-linked, charge-modified biopolymer prepared using a conventional method.

An additional aspect of the present invention includes a cross-linked, charge-modified biopolymer having an increased porosity and/or pore size compared to a cross-linked, charge-modified biopolymer prepared using a conventional method.

A further aspect of the present invention includes a method of absorbing a fluid comprising contacting a cross-linked, charge-modified biopolymer of the present invention with the fluid, thereby absorbing the fluid.

Another aspect of the present invention includes a cross-linked, charge-modified biopolymer having an increased salt uptake and/or metal chelation property compared to a cross-linked, charge-modified biopolymer prepared using a conventional method.

Another aspect of the present invention includes a method of reducing the amount of a salt and/or metal in a solution comprising contacting the cross-linked, charge-modified biopolymer of the present invention with a solution comprising a salt and/or metal, wherein the salt and/or metal binds to the cross-linked, charge-modified biopolymer, thereby reducing the amount of the salt and/or metal in the solution.

The foregoing and other aspects of the present invention will now be described in more detail with respect to other embodiments described herein. It should be appreciated that the invention can be embodied in different forms and should not be construed as limited to the embodiments set forth herein. Rather, these embodiments are provided so that this disclosure will be thorough and complete, and will fully convey the scope of the invention to those skilled in the art.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1A is a schematic of a heterogeneous phase reaction.

FIG. 1B is a schematic of a homogeneous phase reaction.

FIG. 2 illustrates a parallel twin screw extruder with multiple injection and reaction zones according to embodiments of the present invention.

FIG. 3 illustrates FTIR spectra for unmodified hemicellulose and charge-modified hemicellulose according to embodiments of the present invention.

FIG. 4 illustrates FTIR spectra for unmodified pectin and charge-modified pectin according to embodiments of the present invention.

FIG. 5 illustrates FTIR spectra for unmodified soy protein and charge-modified soy protein according to embodiments of the present invention.

FIG. 6 illustrates exemplary screw configurations according to embodiments of the present invention.

FIG. 7A shows a SEM image of a commercially available cationic starch at 33×.

FIG. 7B shows a SEM image of the commercially available cationic starch at 1000×.

FIG. 7C shows a SEM image of an EDS chlorine map of the commercially available cationic starch.

FIG. 7D shows a SEM image of a cationic starch prepared according to methods of the present invention at 33×.

FIG. 7E shows a SEM image of the cationic starch prepared according to methods of the present invention at 1000×.

FIG. 7F shows a SEM image of an EDS chlorine map of the cationic starch prepared according to methods of the present invention.

DETAILED DESCRIPTION

The present invention will now be described more fully hereinafter. This invention may, however, be embodied in different forms and should not be construed as limited to the embodiments set forth herein. Rather, these embodiments are provided so that this disclosure will be thorough and complete, and will fully convey the scope of the invention to those skilled in the art.

The terminology used in the description of the invention herein is for the purpose of describing particular embodiments only and is not intended to be limiting of the invention. As used in the description of the invention and the appended claims, the singular forms “a”, “an” and “the” are intended to include the plural forms as well, unless the context clearly indicates otherwise.

Unless otherwise defined, all terms (including technical and scientific terms) used herein have the same meaning as commonly understood by one of ordinary skill in the art to which this invention belongs. It will be further understood that terms, such as those defined in commonly used dictionaries, should be interpreted as having a meaning that is consistent with their meaning in the context of the present application and relevant art and should not be interpreted in an idealized or overly formal sense unless expressly so defined herein. The terminology used in the description of the invention herein is for the purpose of describing particular embodiments only and is not intended to be limiting of the invention. All publications, patent applications, patents and other references mentioned herein are incorporated by reference in their entirety. In case of a conflict in terminology, the present specification is controlling.

Also as used herein, “and/or” refers to and encompasses any and all possible combinations of one or more of the associated listed items, as well as the lack of combinations when interpreted in the alternative (“or”).

Unless the context indicates otherwise, it is specifically intended that the various features of the invention described herein can be used in any combination. Moreover, the present invention also contemplates that in some embodiments of the invention, any feature or combination of features set forth herein can be excluded or omitted. To illustrate, if the specification states that a complex comprises components A, B and C, it is specifically intended that any of A, B or C, or a combination thereof, can be omitted and disclaimed.

As used herein, the transitional phrase “consisting essentially of” (and grammatical variants) is to be interpreted as encompassing the recited materials or steps “and those that do not materially affect the basic and novel characteristic(s)” of the claimed invention. See, In re Herz, 537 F.2d 549, 551-52, 190 U.S.P.Q. 461, 463 (CCPA 1976) (emphasis in the original); see also MPEP § 2111.03. Thus, the term “consisting essentially of” as used herein should not be interpreted as equivalent to “comprising.”

The term “about,” as used herein when referring to a measurable value, such as, for example, an amount or concentration and the like, is meant to refer to variations of up to ±20% of the specified value, such as, but not limited to, ±20%, ±15%, ±10%, ±5%, ±1%, ±0.5%, or even ±0.1% of the specified value, as well as the specified value. For example, “about X” where X is the measurable value, is meant to include X as well as variations of ±20%, ±15%, ±10%, ±5%, ±1%, ±0.5%, or even ±0.1% of X. A range provided herein for a measureable value may include any other range and/or individual value therein.

According to some embodiments of the present invention, provided herein are modified biopolymers, such as, charge-modified biopolymers, cross-linked biopolymers, and/or cross-linked, charge-modified biopolymers. The cross-linked, charged-modified biopolymers of the present invention may comprise one biopolymer that has been charge-modified and cross-linked. In some embodiments, the cross-linked, charged-modified biopolymers of the present invention may comprise two or more different biopolymers that are cross-linked and at least one of the biopolymers has been charge-modified. The two or more different biopolymers may be cross-linked with each other. In certain embodiments, a cross-linked, charge-modified biopolymer may comprise two different biopolymers that are cross-linked and both of the biopolymers may be charge-modified.

A “biopolymer” as used herein refers to a polymer that has at least one free amine and/or hydroxyl group present on a majority of the monomeric units of the polymer and is a polymer produced by a living organism or a derivative thereof. In some embodiments, a free amine and/or hydroxyl group may be present on each of the monomeric units of the polymer backbone. Exemplary biopolymers include, but are not limited to, proteins and/or polysaccharides. As one of ordinary skill in the art will understand, a biopolymer may be synthetically obtained (e.g., through laboratory synthesis) and/or obtained and/or derived from nature (e.g., from a living or previously living organism). Therefore, the biopolymer may be the same as a polymer found in nature (i.e., a native biopolymer) or may be a derivative thereof. For example, a biopolymer of the present invention may be a derivative of a polymer produced by a living organism, the derivative caused by the synthetic method used to obtain or isolate the biopolymer from nature. In some embodiments, a biopolymer may be a polymer produced by bacteria and/or microbes.

Further exemplary biopolymers include, but are not limited to, starches (including amylose and/or amylopectin), chitosans, hemicelluloses, lignins, celluloses, chitins, alginates, dextrans, pullanes, polyhydroxyalkanoates, fibrins, cyclodextrins, proteins (e.g., soy protein), polysaccharides (e.g., pectin), and/or polylactic acids.

A biopolymer used in a method of the present invention may have a moisture content of about 20% by weight or less. In some embodiments, the biopolymer may have a moisture content of about 20%, 15%, 10%, 5%, or less by weight. In certain embodiments, the biopolymer may have a moisture content in a range of about 5% to about 20% by weight or about 10% to about 15% by weight. In some embodiments, a method of the present invention utilizes a biopolymer, such as, for example, starch, having a moisture content of about 20% by weight or less, and the biopolymer may be in powder form.

A biopolymer used in a method of the present invention may have a molecular weight of about 10,000 Daltons or more. In some embodiments, the biopolymer may have a molecular weight of about 10,000; 20,000; 30,000; 40,000, 50,000; 60,000; 70,000; 80,000; 90,000; 100,000; 200,000; 300,000; 400,000; 500,000; 600,000; 700,000; 800,000; 900,000; 1,000,000; 2,000,000; 3,000,000, 4,000,000 Daltons or more. In certain embodiments, the biopolymer may have a molecular weight of about 50,000 Daltons or more. In some embodiments, the biopolymer may have a molecular weight of about 100,000 Daltons to about 4,000,000 Daltons, about 500,000 Daltons to about 3,000,000 Daltons, or about 1,000,000 Daltons to about 2,000,000 Daltons. In some embodiments, when only one biopolymer is used to prepare a modified biopolymer of the present invention (e.g., a cross-linked, charge-modified biopolymer), the biopolymer may have a molecular weight of greater than about 50,000 Daltons. In some embodiments, when two or more different biopolymers are used to prepare a modified biopolymer of the present invention (e.g., a cross-linked, charge-modified biopolymer), at least one of the two or more different biopolymers may have a molecular weight of about 10,000 Daltons or more, such as, for example, about 20,000; 30,000; 40,000, 50,000 Daltons or more. In certain embodiments, a modified biopolymer of the present invention (e.g., a cross-linked, charge-modified biopolymer) may be prepared using a biopolymer having a molecular weight of greater than about 50,000 Daltons optionally with a second different biopolymer having a molecular weight of greater than about 10,000 Daltons. In some embodiments, the biopolymer may be polydisperse.

In some embodiments, the biopolymer used in a method of the present invention may be a starch. Exemplary starches include, but are not limited to, potato starch, wheat starch, tapioca starch, cassava starch, rice starch, corn starch, waxy corn starch, waxy wheat starch, waxy rice starch, waxy sorghum starch, waxy cassava starch, waxy barley starch, and/or waxy potato starch. The starch may have an amylopectin content of about 70% w/w or more and an amylose content of about 30% w/w or less. In certain embodiments, the starch may have an amylopectin content of about 70%, 75%, 80%, 85%, 90%, 95% w/w or more and an amylose content of about 30%, 25%, 20%, 15%, 10%, 5% w/w or less. In some embodiments, the starch may have an amylopectin content of less than 90%, such as, for example, about 85%, 80%, 75%, 70%, 65%, 60%, 55%, 50%, 45%, 40%, 35%, 30%, 25%, 20%, 15%, 10%, etc. In some embodiments, starch may have an amylopectin content in a range of about 10% to about 85%, such as, for example, about 25% to about 85% or about 50% to about 80%.

In some embodiments, the starch may be dissolvable in water (e.g., pre-gelatinized starch). In certain embodiments, the starch may be steam exploded to form a pre-gelatinized starch. In some embodiments, a starch used in a method of the present invention may have a reduced degree of crystallinity compared to a native starch. In certain embodiments, the biopolymer used in a method of the present invention may be a chitosan. The chitosan may have a degree of deacetylation of about 50% to about 100%. In some embodiments, the chitosan may have a degree of deacetylation of about 50%, 55%, 60%, 65%, 70%, 75%, 80%, 85%, 90%, 95%, or 100%. In certain embodiments, the chitosan may have a degree of deacetylation in a range of about 70% to about 100% or greater than about 80%. In some embodiments, the chitosan may have a molecular weight of greater than about 80,000 Daltons.

A biopolymer used in a method of the present invention may be charge-modified according to a method described herein (e.g., by reacting the biopolymer with a charge-modifying agent in a homogeneous reaction blend). However, as one of skill in the art will recognize, a biopolymer may naturally carry a charge (i.e., the biopolymer may natively be charged in that the charge is present on the biopolymer not through a method of the present invention). Thus, a method of the present invention may change the charge present on a biopolymer (e.g., type and/or amount of charge). In some embodiments, a charge-modified biopolymer may be soluble (e.g., partially or fully soluble) in a polar solvent, such as, for example, water and/or a polar organic solvent at room temperature and/or a nonpolar solvent at room temperature. In some embodiments, a charge-modified biopolymer of the present invention may be at least 70% soluble in a polar and/or nonpolar solvent at room temperature. Solubility may be used as an indication and/or characteristic of the degree of charge modification.

“Charge-modifying agent” as used herein refers to a molecule or compound comprising one moiety that may react with an amine and/or hydroxyl group of the biopolymer and a second moiety that may be positively charged or negatively charged under suitable conditions, such as, for example, at a certain pH. “Moiety” as used herein, refers to a portion of a molecule or compound having a particular functional or structural feature. For example, a moiety may comprise a functional group or a reactive portion of a compound. As those of skill in the art recognize, a strong acidic moiety (e.g., —SO₃H) or a weak acidic moiety (e.g., —COOH) may form a negatively charged moiety and a strong basic moiety (e.g., —NH₃OH) or a weak basic moiety (—NH₂) may form a positively charged moiety.

The charge-modifying agent may comprise at least one moiety that may be a positively charged group, such as, but not limited to, a primary amine, secondary amine, tertiary amine, quaternary ammonium, sulfonium, and/or phosphonium group. Exemplary charge-modifying agents that can have a positively charged moiety include, but are not limited to, ethylene imine, N-(2-hydroxyethyl) ethylene imine, cyanamide, beta-morpholinoethylchloride, beta-diethyl aminoethylchloride, S-diethyl amino 1,2-epoxypropane dimethyl aminoethyl methacrylate, epoxy 3-methyl ammonium, glycidyltrimethylammonium chloride (e.g., QUAB® 151), N-(2,3-epoxypropyl) trimethyl ammonium chloride, (4-chlorobutene-2) trimethyl ammonium chloride, 2-chloroethyl methyl ethyl sulfonium iodide, and/or Z-chloroethyl tributylphosphonium chloride. In some embodiments, the charge-modifying agent comprises a tertiary amino alkyl group, a hydroxyalkyl group, a quaternary ammonium alkyl group, or a hydroxyalkyl group.

In some embodiments, a positively charged moiety may be introduced into and/or onto a biopolymer by reacting the biopolymer and charge-modifying agent in a homogeneous reaction blend, optionally in the presence of a catalyst. This reaction may be a dry melt process and/or may be an etherification or esterification reaction.

The charge-modifying agent may comprise at least one moiety that may be a negatively charged group, such as, but not limited to, a carboxyl, sulfonate, sulfate, and/or a phosphate group (e.g., sodium tripolyphosphate). Exemplary charge-modifying agents that can have a negatively charged moiety include, but are not limited to, acids (e.g., citric acid, glacial acetic acid, ethylenediaminetetraacetic acid (EDTA), and/or diethylene triamine pentaacetic acid (DTPA)); mono-halogen substituted fatty acids (e.g., monochloroacetic acid); acetates (e.g., sodium monochloroacetate); anhydrides (e.g., succinic anhydride, maleic anhydride, citraconic anhydride, and/or octenyl succinicanhydride); alkyl esters of acrylic acid, crotonic acid or itaconic acid (e.g., methyl and ethyl esters of acrylic acid, crotonic acid or itaconic acid); acrylonitrile; sodium periodate; sulfones; and/or sulfonic acids (e.g., halo alkane sulfonic acids, chlorooxypropane sulfonic acid, epoxypropane sulfonic acid, chlorooxypropane sulfonic acid, epoxypropane sulfonic acid, ethene sulfonic acid, and/or salts thereof).

In some embodiments, a negatively charged moiety may be introduced into a biopolymer by reacting the biopolymer and charge-modifying agent in a homogeneous reaction blend in the presence an alkaline catalyst. In certain embodiments, the charge-modifying agent may be acrylonitrile and the reaction of the biopolymer and acrylonitrile in the presence of an alkaline catalyst may be followed by hydrolysis of the cyanoethyl groups. When the charge-modifying agent is sodium periodate, the reaction with the biopolymer may be followed by a treatment to transform the carbonyl groups into carboxyl groups, such as, but not limited to, by treating with sodium chlorite, and/or by a treatment with sodium bisulfite and/or potassium bisulfite. In certain embodiments, both carboxyl and sulfonate groups may be introduced into a biopolymer by reacting the biopolymer with an anhydride of an unsaturated acid (e.g., maleic acid) and a bisulfite. The bisulfite may be reacted with the unsaturated bond of the polysaccharide half ester.

In some embodiments, the charge-modifying agent may react with an amine and/or hydroxyl group of a biopolymer to provide a charge-modified biopolymer. The charge-modified biopolymer may be cationic (i.e., have a net positive charge) or may be anionic (i.e., have a net negative charge). In some embodiments, the charge-modified biopolymer may contain both positively and negatively charged moieties.

A biopolymer used in a method of the present invention may be cross-linked by reacting a cross-linking agent with the biopolymer and optionally with at least one different biopolymer that may optionally be charge-modified. In some embodiments, a cross-linking agent may be reacted with at least one charge-modified biopolymer. “Cross-linking agent” as used herein refers to a compound that links two or more biopolymer chains and/or portions of the biopolymer together, the biopolymer optionally being charge-modified. The linkage may be achieved via a covalent bond or an ionic bond. In some embodiments, the linkage may be through a moiety or group of the biopolymer or different biopolymers.

Exemplary cross-linking agents include, but are not limited to, epichlorohydrin, glutaraldehyde, oxalic acid, malonic acid, succinic acid, glutaric acid, adipic acid, pimelic acid, fumaric acid, maleic acid, malic acid, tartartic acid, sodium trimetaphosphate, sodium tripolyphosphate, ionic cross-linkers (e.g., calcium chloride, calcium hydroxide, etc.), poly(ethylene glycol) diglycidyl ether (PEGDE), poly(propylene glycol) diglycidyl ether (PPGDE), and/or an anhydride, such as, for example, succinic anhydride and maleic anhydride. In some embodiments, the cross-linking agent is non-toxic.

Without wishing to be bound to any particular theory, in some embodiments, a charge-modifying agent, such as, for example, citric acid, when heated inside an extruder may dehydrate to yield an anhydride. The free hydroxyl groups from a biopolymer, such as, for example, starch, present in the reaction mixture may react with the anhydride to form starch citrate. Further, without wishing to be bound to any particular theory, in some embodiments, additional dehydration of the biopolymer and/or charge-modified biopolymer may allow for cross-linking of the biopolymer and/or charge-modified biopolymer to occur. In some embodiments, cross-linking of the biopolymer and/or charge-modified biopolymer may be achieved due to the heat inside the extruder and/or during a post treatment process, such as, for example, a thermal post-treatment process. In some embodiments, a charge-modified biopolymer may be prepared using a ring-opening polymerization of anhydrous acids.

A modified biopolymer of the present invention (e.g., a cross-linked, charge-modified biopolymer) may comprise a plurality of pores or void spaces formed therein. The pores or void spaces may have an average diameter of about 0.1 micron to about 500 microns, such as, but not limited to, about 10 microns to about 500 microns, about 50 microns to about 500 microns, about 100 microns to about 400 microns, or about 250 microns to about 500 microns. In certain embodiments, the pores or void spaces may have an average diameter of about 0.1 micron, 1 micron, 10 microns, 25 microns, 50 microns, 100 microns, 150 microns, 200 microns, 250 microns, 300 microns, 350 microns, 400 microns, 450 microns, or 500 microns.

In some embodiments, a modified biopolymer of the present invention (e.g., a cross-linked, charge-modified biopolymer) has a net positive charge (i.e., is cationic) or a net negative charge (i.e., is anionic). In certain embodiments, the modified biopolymer (e.g., a cross-linked, charge-modified biopolymer) is a polyampholyte. In some embodiments, the modified biopolymer may be a polyelectrolyte, which may be hydrophilic (e.g., due to the number of ionizable groups present on the modified biopolymer). In some embodiments, a modified biopolymer of the present invention (e.g., a cross-linked, charge-modified biopolymer) may be a superabsorbent. In some embodiments, a superabsorbent of the present invention, may absorb a fluid in an amount of about 15 times or more (e.g., 20×, 30×, 40×, 50×, 100×, etc.) relative to its weight. A superabsorbent, in some embodiments, may absorb a 0.9% saline solution in an amount of about 20 times or more (e.g., 25×, 30×, etc.) at room temperature and/or water in an amount of about 35 times or more (e.g., 40×, 45×, etc.) at room temperature. In some embodiments, a cross-linked, charge-modified biopolymer of the present invention is charge-modified and cross-linked in an extruder. Some embodiments of the present invention may provide a cross-linked, charge-modified biopolymer in a one step extrusion process.

A modified biopolymer of the present invention (e.g., a cross-linked, charge-modified biopolymer) may be a biosorbent and/or may be biodegradable. A “biosorbent” as used herein may refer to an absorbent (e.g., that may be utilized in the removal of a fluid) and/or an adsorbent (e.g., that may be utilized as an ion exchange material and/or metal chelating material). In some embodiments, a biosorbent may be a superabsorbent.

A modified biopolymer of the present invention (e.g., a cross-linked, charge-modified biopolymer and/or charge-modified biopolymer) may have a charge density of about 3 meq/g or more as determined by titration. For example, in some embodiments, charge density may be determined by titration as described in Example 1.1. In some embodiments, the modified biopolymer may have a charge density of about 3, 3.5, 4, 4.5, 5, 5.5, 6, 6.5, 7, 7.5, 8, 8.5, 9, 9.5, 10 meq/g or more as determined by titration. In certain embodiments, the modified biopolymer may have a charge density of at least about 5 meq/g as determined by titration.

In some embodiments, a method of the present invention may provide a modified biopolymer (e.g., a cross-linked, charge-modified biopolymer and/or charge-modified biopolymer) having the charge modification substantially uniformly distributed throughout the bulk of the modified biopolymer. Thus, the modified biopolymer may have a substantially uniform charge density. In some embodiments, the uniformity of the charge density of a modified biopolymer may be determined by evaluating the presence of insoluble materials after exposure of the modified biopolymer to a solvent, such as, for example water. Observation of particles (such as, for example, 1-10 μm particles) may indicate the lack of charge modification within the particles and/or modified biopolymer. In some embodiments, charge density distribution on a modified biopolymer may be determined and/or evaluated using one or more spectrographic analytical techniques such as, but not limited to, EDS, EPS, and/or TOF-SIMS of the charged moiety's counter ion. In some embodiments, an uneven distribution of counter ions and/or the presence of particles (e.g., 1-10 μm particles) lacking the counter ion indicates non-uniformity and/or inhomogeneity in regard to the distribution of the charge on the modified biopolymer.

In some embodiments, the modified biopolymer may have an increased charge density and/or degree of cross-linking compared to a modified biopolymer (e.g., a cross-linked, charge-modified biopolymer) prepared using a conventional method. “Conventional method” as used herein in reference to a method for preparing a modified biopolymer refers to a method for preparing a modified biopolymer in which the biopolymer is a solid (e.g., a particulate) and a reaction of the biopolymer with at least one reactant in the method occurs at a solid interface of the biopolymer. In some embodiments, a conventional method may be a method that does not involve forming a homogeneous reaction blend and/or that does not involve a melt extrusion process, such as a reactive extrusion process. In some embodiments, a conventional method may be a semi-dry process, a multi-phase process, a process having a liquid interface with a solid material, and/or a heterogeneous process. In certain embodiments, a conventional method may be a heterogeneous wet chemistry method and/or a multi-phase process.

The modified biopolymer may have a charge density and/or degree of cross-linking that is increased by at least about 5% or more compared to a modified biopolymer prepared using a conventional method. In some embodiments, the modified biopolymer may have a charge density and/or degree of cross-linking that is increased by at least about 5%, 10%, 15%, 20%, 25%, 30%, 35%, 40%, 45%, 50%, 55%, 60%, 65%, 70%, 75%, 80%, 85%, 90%, 95%, 100%, 150%, 200%, or more compared to a modified biopolymer prepared using a conventional method.

In some embodiments, the degree or amount of cross-linking present in a modified biopolymer of the present invention (e.g., a cross-linked, charge-modified biopolymer and/or cross-linked biopolymer) may provide mechanical rigidity to the modified biopolymer and/or correlate with the degree of mechanical rigidity in the modified biopolymer.

In some embodiments, a modified biopolymer of the present invention (e.g., a cross-linked, charge-modified biopolymer) may have a degree of substitution of about 0.01 or more, such as, for example, in a range of about 0.01 to about 0.3. For example, in some embodiments, the modified biopolymer may have a degree of substitution of about 0.01, 0.02, 0.03, 0.04, 0.05, 0.06, 0.07, 0.08, 0.09, 0.1, 0.15, 0.2, 0.25, 0.3, or more. In some embodiments, a modified biopolymer may have a degree of substitution in a range of about 0.09 to about 0.3 or about 0.1 to about 0.25. In some embodiments, the degree of substitution may be measured by nitrogen content.

In some embodiments, a modified biopolymer of the present invention (e.g., a cross-linked, charge-modified biopolymer) may have a free swell capacity (FSC) of about 5 g/g or more, such as, for example, in a range of about 5 g/g to about 100 g/g. For example, in some embodiments, the modified biopolymer may have a FSC of about 5, 6, 7, 8, 9, 10, 11, 12, 13, 14, 15, 16, 17, 18, 19, 20, 21, 22, 23, 24, 25, 26, 27, 28, 29, 30, 31, 32, 33, 34, 35, 36, 37, 38, 39, 40, 41, 42, 43, 44, 45, 46, 47, 48, 49, 50, 51, 52, 53, 54, 55, 56, 57, 58, 59, 60, 61, 62, 63, 64, 65, 66, 67, 68, 69, 70, 71, 72, 73, 74, 75, 76, 77, 78, 79, 80, 81, 82, 83, 84, 85, 86, 87, 88, 89, 90, 91, 92, 93, 94, 95, 96, 97, 98, 99, 100, or more.

In some embodiments, a modified biopolymer of the present invention (e.g., a cross-linked, charge-modified biopolymer) may have a Centrifuge Retention Capacity (CRC) of about 1 g/g or more, such as, for example, in a range of about 1 g/g to about 60 g/g. For example, in some embodiments, the modified biopolymer may have a CRC of about 1, 2, 3, 4, 5, 6, 7, 8, 9, 10, 11, 12, 13, 14, 15, 16, 17, 18, 19, 20, 21, 22, 23, 24, 25, 26, 27, 28, 29, 30, 31, 32, 33, 34, 35, 36, 37, 38, 39, 40, 41, 42, 43, 44, 45, 46, 47, 48, 49, 50, 51, 52, 53, 54, 55, 56, 57, 58, 59, 60, or more.

A modified biopolymer of the present invention (e.g., a cross-linked, charge-modified biopolymer) may comprise a plurality of pores and/or void spaces. The modified biopolymer may have an increased porosity and/or pore size compared to a modified biopolymer prepared using a conventional method. The porosity may be increased by increasing the number of pores or void spaces. The pores or void spaces may be substantially the same size (e.g., varying in size or diameter by less than about 20%) or may be different sizes. The modified biopolymer may have a porosity and/or pore size that is increased by at least about 5% or more compared to a modified biopolymer prepared using a conventional method. In some embodiments, the modified biopolymer may have a porosity and/or pore size that is increased by at least about 5%, 10%, 15%, 20%, 25%, 30%, 35%, 40%, 45%, 50%, 55%, 60%, 65%, 70%, 75%, 80%, 85%, 90%, 95%, 100%, 150%, 200%, or more compared to a modified biopolymer prepared using a conventional method.

In some embodiments, the modified biopolymer may have a more uniform porosity and/or pore size compared to a modified biopolymer prepared using a conventional method. A more uniform porosity may include a more uniformly or evenly dispersed number of pores or void spaces throughout the modified biopolymer. In some embodiments, a more uniform pore size may include a more uniform diameter of the pores or void spaces throughout the modified biopolymer. In certain embodiments, the porosity and/or pore size of the modified biopolymer may be more uniform compared to the porosity and/or pore size of a modified biopolymer prepared using a conventional method, and may vary by less than about 20%, such as, for example, by about 20%, 15%, 10%, 5% or less, as determined by comparing two or more defined areas of the modified biopolymer compared to two or more defined areas of the modified biopolymer prepared using a conventional method.

A modified biopolymer of the present invention (e.g., a cross-linked, charge-modified biopolymer) may sequester, bind, absorb, chelate, uptake, adsorb, and/or the like a fluid (e.g., water, hydrocarbons, oils, alcohols, aqueous solutions, non-aqueous solutions, ionic solutions such as salt solutions, biological fluids such as blood and/or urine, gases, waste water, and/or fracking fluids), a charged species (e.g., ions such as potassium ions (K⁺), calcium ions (Ca²⁺), sodium ions (Na⁺), chloride ions (Cl⁻), fluoride ions (F⁻), phosphite ions (PO₃ ³⁻), sulfate ions (SO₄ ²⁻), sulfite ions (SO₃ ²⁻), phosphate ions (PO₄ ³⁻), polyatomic ions, and/or metal ions; charged peptides, polypeptides, nucleic acids, and/or oligonucleotides; and the like), and/or a metal (e.g., lead, mercury, cadmium, arsenic, copper, chromium, thallium, selenium, zinc, calcium, magnesium, silver, boron, and the like). In some embodiments, a modified biopolymer of the present invention (e.g., a cross-linked, charge-modified biopolymer) may physically adsorb a species present in a fluid, such as, but not limited to an ionic species and/or a metal. The species may be dissolved in the fluid. In certain embodiments, a modified biopolymer may bind, such as, for example, via hydrogen bonding, covalent bonding, van der waals/adsorptive binding, and/or ionic bonding, a fluid, charged species, and/or metal.

In certain embodiments, a modified biopolymer of the present invention (e.g., a cross-linked, charge-modified biopolymer) may sequester, bind, absorb, chelate, uptake, adsorb, and/or the like an ion and/or a metal. The metal may be in an ionized form, such as in the form of a salt. As those skilled in the art recognize, a metal may exist in a number of ionized forms, such as, monovalent, divalent, polyvalent, anionic, and/or cationic forms. Further exemplary ions and/or metals, in any ionized form, that a modified biopolymer of the present invention may sequester, bind, absorb, chelate, uptake, adsorb, and/or the like include, but are not limited to, sodium, potassium, lithium, ammonium, barium, strontium, manganese, silver, cesium, zinc, cadmium, selenium, calcium, magnesium, iron, radium, mercury, copper, lead, nickel, chromium, arsenic, gold, uranium, chloride, bromide, nitrate, iodide, carbonate, sulphate, and/or phosphate.

In some embodiments, a modified biopolymer of the present invention (e.g., a cross-linked, charge-modified biopolymer) may sequester, bind, absorb, chelate, uptake, adsorb, and/or the like an organic. Exemplary organics include, but are not limited to, toluene, xylenes, benzene, ethylbenzene, trimethylbenzene, acetone, and/or methanol.

A modified biopolymer of the present invention (e.g., a cross-linked, charge-modified biopolymer) may sequester, bind, absorb, chelate, uptake, adsorb, and/or the like an increased amount or concentration of a fluid, a charged species, and/or a metal compared to a modified biopolymer prepared using a conventional method. The modified biopolymer may sequester, bind, absorb, chelate, uptake, adsorb, and/or the like an increased amount or concentration of a fluid, charged species, and/or a metal by at least about 5% or more compared to a modified biopolymer prepared using a conventional method. In some embodiments, the modified biopolymer may sequester, bind, absorb, chelate, uptake, adsorb, and/or the like an increased amount or concentration of a fluid, charged species, and/or a metal by at least about 5%, 10%, 15%, 20%, 25%, 30%, 35%, 40%, 45%, 50%, 55%, 60%, 65%, 70%, 75%, 80%, 85%, 90%, 95%, 100%, 150%, 200%, or more compared to a modified biopolymer prepared using a conventional method.

In some embodiments, a modified biopolymer of the present invention may comprise starch and chitosan. The starch and chitosan may both be charged-modified and cross-linked with each other to form a cross-linked, charged-modified starch-chitosan biopolymer.

According to some embodiments of the present invention, a method for producing a charge-modified biopolymer may be provided. The method may comprise reacting a biopolymer and at least one charge-modifying agent in a homogeneous reaction blend to form a charge-modified biopolymer. In some embodiments, the method may comprise combining the biopolymer and at least one charge-modifying agent, optionally with a plasticizer and/or catalyst, to form a homogenous reaction blend. In some embodiments, the method may comprise reacting two or more different biopolymers with a charge-modifying agent in a homogeneous reaction blend. Optionally, at least one of the two or more different biopolymers may be charge-modified (e.g., according to a method of the present invention) prior to the reacting step.

According to some embodiments of the present invention, a method for producing a cross-linked biopolymer may be provided. The method may comprise reacting a biopolymer and at least one cross-linking agent in a homogeneous reaction blend to form a cross-linked biopolymer. In some embodiments, the method may comprise combining the biopolymer and at least one cross-linking agent, optionally with a plasticizer and/or catalyst, to form a homogenous reaction blend. In some embodiments, the method may comprise reacting two or more different biopolymers with a cross-linking agent in a homogeneous reaction blend.

According to some embodiments of the present invention, a method for producing a cross-linked, charge-modified biopolymer may be provided. The method may comprise reacting a biopolymer and at least one charge-modifying agent in a homogenous reaction blend to form a charge-modified biopolymer and cross-linking the charge-modified biopolymer in the homogeneous reaction blend to form a cross-linked, charge-modified biopolymer. Some embodiments may include reacting two or more different biopolymers with the at least one charge-modifying agent in the homogeneous reaction blend to form at least one charge-modified biopolymer. In some embodiments, the charge-modified biopolymer may be cross-linked to one or more different biopolymers in the homogeneous reaction blend, and the one or more different biopolymers may optionally be charge-modified, such as, for example, prior to a combining, reacting, and/or cross-linking step. In some embodiments, a charge-modified biopolymer prepared according to a method of the present invention is used to prepare a cross-linked, charge-modified biopolymer of the present invention. In some embodiments, the biopolymer and the at least one charge-modifying agent may be combined to form a homogeneous reaction blend.

In some embodiments, one or more steps of a method of the present invention (e.g., a combining, reacting, and/or cross-linking step) may occur simultaneously and/or sequentially with another step in the method. For example, in some embodiments, a reacting step to form a charged-modified biopolymer of the present invention may occur simultaneously with a cross-linking step to form a cross-linked, charge-modified biopolymer of the present invention. A further example includes, in some embodiments, that a cross-linking step to form a cross-linked, charge-modified biopolymer of the present invention may occur after a reacting step to form a charged-modified biopolymer has occurred. In some embodiments, a reacting and cross-linking step occur in different reaction zones of an extruder.

In some embodiments, a method for producing a cross-linked, charge-modified biopolymer may comprise combining a first charge-modified biopolymer and a second charge-modified biopolymer that is different than the first charge-modified biopolymer, optionally with a plasticizer, cross-linking agent, and/or catalyst, to form a homogeneous reaction blend, and cross-linking the first and second charge-modified biopolymers in the homogeneous reaction blend to form a cross-linked, charge-modified biopolymer. The first and/or second charge-modified biopolymers may be charge-modified according to a method of the present invention.

Some embodiments include a method for producing a cross-linked, charge-modified biopolymer comprising: combining a first biopolymer, a second biopolymer that is different than the first biopolymer, at least one charge-modifying agent, a plasticizer, and optionally a catalyst to form a homogenous reaction blend; reacting the first biopolymer and second biopolymer with the at least one charge-modifying agent to form a charge-modified first biopolymer and a charge-modified second biopolymer; and cross-linking the charge-modified first biopolymer and charge-modified second biopolymer to form a cross-linked, charge-modified biopolymer.

In some embodiments, a method for producing a cross-linked, charge-modified biopolymer comprises: combining a first biopolymer, a first charge-modifying agent, and optionally a catalyst to form a homogeneous reaction blend comprising a charge-modified first biopolymer; adding a charge-modified second biopolymer and a plasticizer to the homogeneous reaction blend comprising the charge-modified first biopolymer; and cross-linking the charge-modified first biopolymer and charge-modified second biopolymer to form a cross-linked, charge-modified biopolymer. In some embodiments, the charge-modified second biopolymer is prepared according to a method of the present invention.

Some embodiments include a method for producing a cross-linked, charge-modified biopolymer comprising: combining a first biopolymer, a first charge-modifying agent, and optionally a catalyst to form a charge-modified first biopolymer; forming a homogeneous reaction blend comprising the charged-modified first biopolymer, a charged-modified second biopolymer, and a plasticizer; and cross-linking the charge-modified first biopolymer and charged-modified second biopolymer to form a cross-linked, charge-modified biopolymer. In some embodiments, the charge-modified second biopolymer is prepared according to a method of the present invention.

In some embodiments, a method for producing a cross-linked, charge-modified biopolymer comprises: forming a homogenous reaction blend comprising a first biopolymer, a second biopolymer that is optionally charged-modified, and at least one charge-modifying agent; reacting the first biopolymer and the at least one charge-modifying agent in the homogenous reaction blend to form a charge-modified biopolymer; and cross-linking the charge-modified biopolymer and the second biopolymer in the homogeneous reaction blend to form a cross-linked, charge-modified biopolymer. In some embodiments, the second biopolymer may be charge-modified according to a method of the present invention.

In some embodiments, a method for producing a cross-linked, charge-modified biopolymer comprises: forming a first homogenous reaction blend comprising a first biopolymer and at least one charge-modifying agent; reacting the first biopolymer and the at least one charge-modifying agent in the first homogenous reaction blend to form a charge-modified biopolymer; combining the charge-modified biopolymer with a second biopolymer that is optionally charge-modified to form a second homogeneous reaction blend; and cross-linking the charge-modified biopolymer and second biopolymer in the second homogeneous reaction blend to form a cross-linked, charge-modified biopolymer. In some embodiments, the second biopolymer may be charge-modified according to a method of the present invention.

In some embodiments, a method for producing a modified biopolymer of the present invention (e.g., a cross-linked, charge-modified biopolymer) may occur and/or be carried out in a continuous process. In some embodiments, the reacting and/or cross-linking steps may occur and/or be carried out in a continuous process. A continuous process is one that does not involve intermediate steps that stop a reaction in process. Exemplary intermediate steps include, but are not limited to, changing a buffer or providing a wash step before obtaining the product. The continuous process may be carried out or performed in an extruder optionally using a reactive extrusion process. For example, a continuous process includes a process in which all reactants are added to an extruder either at the same time or different times and the process occurs continuously (i.e. without stopping for intermediate steps) until the modified biopolymer is extruded. A continuous process may also include a step in a method of the present invention that is carried out or performed in an extruder, such as a reacting and/or cross-linking step.

In some embodiments, a method of the present invention may comprise a continuous process followed by a non-continuous process, such as, but not limited to, a post-treatment step. In certain embodiments, a method of the present invention may comprise a continuous process, a non-continuous process (e.g., a batch process), and optionally a subsequent continuous process. In some embodiments, a method of the present invention may comprise a continuous process to prepare a charge-modified biopolymer (e.g., a charge-modified starch), and then the charge-modified biopolymer may undergo a post-treatment, which may optionally be a batch process. The method may further comprise another continuous process in which the charged-modified biopolymer may be reacted with another biopolymer (e.g., chitosan), which may optionally be charge-modified.

A “reactive extrusion process” as used herein refers to a process in which a biopolymer is both chemically and physically modified. A reactive extrusion process may provide for a chemical modification of a biopolymer, such as, but not limited to, grafting onto the biopolymer, cross-linking of the biopolymer, functionalization of the biopolymer, and/or charge-modification of the biopolymer. In some embodiments, a reactive extrusion process may provide for polymerization and/or branching of a biopolymer. The polymerization and/or branching may be with a different biopolymer to provide a co-polymer. An exemplary physical modification may be changing the form of the biopolymer, such as, but not limited to, from a powder, particulate, and/or solid form to a molten or melted form.

At least one charge-modifying agent may be present in a homogeneous reaction blend in an amount of about 5% to about 200% or more by weight of a biopolymer present in the homogeneous reaction blend. In some embodiments, at least one charge-modifying agent may be present in a homogeneous reaction blend in an amount of about 5%, 10%, 20%, 30%, 40%, 50%, 60%, 70%, 80%, 90%, 100%, 110%, 120%, 130%, 140%, 150%, 160%, 170%, 180%, 190%, 200%, or more by weight of a biopolymer present in the homogeneous reaction blend. In some embodiments, at least one charge-modifying agent may be present in a homogeneous reaction blend in an amount of at least about 75% by weight of a biopolymer present in the homogeneous reaction blend. In some embodiments, a method of the present invention may include at least one charge-modifying agent present in a homogeneous reaction blend in an amount of at least about 75% by weight of the biopolymer and provide a modified biopolymer having a charge density of at least 1.5 meq/g of the modified biopolymer.

A homogeneous reaction blend is a melted blend of all the components in a single phase. In some embodiments, a homogeneous reaction blend may be obtained using an extruder. In certain embodiments, a homogeneous reaction blend may be obtained using a reactive extrusion process in an extruder. The homogeneous reaction blend may be in the form of a single liquid phase. A homogeneous reaction blend may provide a uniform distribution of the components or reactants as compared to a conventional method. In some embodiments, a method of the present invention may provide a chemical reaction that occurs more uniformly and/or completely due to the formation of a homogeneous reaction blend as compared to a conventional method. In some embodiments, the biopolymer in the homogeneous reaction blend may be a melted thermoplastic. A biopolymer may react thermo-mechanically and/or chemically with one or more reagents to form a charge-modified biopolymer of the present invention, which may be thermoplastic and/or a viscoelastic material. In some embodiments, a method of the present invention removes hydrogen bonding and/or crystalline domains present in a biopolymer. This may allow for all or substantially all portions of the biopolymer to be available for chemical reaction, such as, for example, charge-modification and/or cross-linking.

In some embodiments, a homogeneous reaction blend may contain a plasticized biopolymer, which may allow for greater access to moieties throughout the biopolymer. In contrast, in a heterogeneous phase reaction (for example, in which modified biopolymers are synthesized by a coating process, in a diluted suspension, or with a concentrated gel solution) there is a limited amount of moieties (e.g., free hydroxyls) exposed to the reagent as the surface moieties are exposed to the reagent, but not the interior moieties are not exposed. The reaction is thus carried out on the surface of the solid granule as shown in FIG. 1A, such as, for example, by direct conversion of either the semi-crystalline granules in aqueous suspension or as a dry process. FIG. 1B shows an exemplary schematic of a homogeneous phase reaction in which a biopolymer in the presence of a plasticizer is a plasticized to obtain thermoplastic behavior. Under the action of thermo-mechanical energy, the starch granule will melt. The plasticizer may be adsorbed to the starch by heating the mixture and destruction of the granule structure of the biopolymer may occur with the introduction of mechanical and heat energy. In the presence of a plasticizer, biopolymer granules may be transferred to a continuous phase and moieties (e.g., hydroxyl free groups) may be available to react with the reagent. In some embodiments, a homogeneous reaction blend may aid in distributing a modification (e.g. a charge-modification) along a biopolymer chain and/or more uniformly throughout a biopolymer in contrast to a conventional method, such as, for example, one in which the modification is only achieved at the surface (e.g. at the surface of a solid biopolymer granule).

In some embodiments, a method of the present invention may provide a modified biopolymer (e.g., a charge-modified biopolymer and/or a cross-linked, charge-modified biopolymer) that lacks a granular structure and/or morphology. In some embodiments, a method of the present invention may destroy or remove the crystalline structure and/or domains of a biopolymer and/or modified biopolymer.

In certain embodiments, a method of the present invention may provide a reaction with faster kinetics than the kinetics of the same reaction in a conventional method. The speed of at least one reaction in a method of the present invention may be increased compared to the speed of the same reaction in a conventional method. In some embodiments, a method of the present invention provides an overall greater speed of reaction to produce a modified biopolymer of the present invention compared to a conventional method. In some embodiments, a plasticizer may be present in the homogeneous reaction blend with a biopolymer and a charge-modifying agent. In some embodiments, a plasticizer may be combined with the biopolymer and the at least one charge-modifying agent to form a homogenous reaction blend. A plasticizer may be present in a homogeneous reaction blend in an amount of about 10% to about 400% or more by weight of a biopolymer present in the homogeneous reaction blend. In some embodiments, a plasticizer may be present in a homogeneous reaction blend in an amount of about 10%, 20%, 30%, 40%, 50%, 60%, 70%, 80%, 90%, 100%, 110%, 120%, 130%, 140%, 150%, 160%, 170%, 180%, 190%, 200%, 210%, 220%, 230%, 240%, 250%, 260%, 270%, 280%, 290%, 300%, 310%, 320%, 330%, 340%, 350%, 360%, 370%, 380%, 390%, 400%, or more by weight of a biopolymer present in the homogeneous reaction blend. In some embodiments, a plasticizer may be present in a homogeneous reaction blend in an amount of at least about 30% or more by weight of a biopolymer (e.g., starch) present in the homogeneous reaction blend. In some embodiments, a plasticizer may be present in a homogeneous reaction blend in an amount of at least about 100% or more by weight of a biopolymer (e.g., chitosan, hemicellulose, pectin, and/or soy protein) present in the homogeneous reaction blend.

In some embodiments, where a reactive plasticizer is used (i.e., a plasticizer that serves as both a plasticizer and a reagent), such as, for example, citric acid, the plasticizer may be present in an amount of about 100%, 125%, 150%, 175%, 200% or more by weight of a biopolymer (e.g., starch) present in the homogeneous reaction blend. In some embodiments, a reactive plasticizer may be present in an amount of about 70% to about 175% by weight of a biopolymer (e.g., starch) present in the homogeneous reaction blend, such as, for example, about 75% to about 100% or about 90% to about 150%. In some embodiments, where a non-reactive plasticizer is used (i.e., a plasticizer that only functions to allow the material to extrude and does not serve as a reagent), such as, for example, water and, at some pHs, glycerol, the plasticizer may be present in amount of about 100% or less, such as, for example, less than 75%, 50%, or 25%. In some embodiments, a non-reactive plasticizer may be present in an amount of about 20% to about 200% by weight of a biopolymer present in the homogeneous reaction blend, such as, for example, about 20% to about 50%, about 75% to about 100%, or about 90% to about 150%.

The plasticizer may reduce the glass transition temperature (T_(g)). In some embodiments, the plasticizer may improve the flexibility, workability, distensibility, and/or processability of a biopolymer and may do so by lowering the glass transition temperature (T_(g)). In certain embodiments, a biopolymer to be extruded by a method of the present invention may not be thermoplastic. Thus, to extrude a biopolymer that is not thermoplastic, the glass transition temperature (T_(g)) must be lowered by addition of a plasticizer.

A plasticizer may reduce the tension of deformation, hardness, density, viscosity and/or electrostatic charge of a biopolymer and at the same time may increase the biopolymer chain flexibility, resistance to fracture and/or dielectric constant. Other properties of the biopolymer may also be affected by the inclusion of a plasticizer, such as, but not limited to, the degree of crystallinity, optical clarity, electric conductivity, fire behavior and/or resistance to biological degradation. In some embodiments, a plasticizer may disrupt hydrogen bonds present in a crystalline structure of the biopolymer and this may lead to the breaking of the crystalline domains that prevent thermal processing.

In some embodiments, the plasticizer may allow for the biopolymer to melt and/or become thermoplastic to provide a single phase. In some embodiments, a plasticizer may lower the T_(g) by solvating the inherent crystallinity of the biopolymer and disrupting hydrogen bonding. This may allow for the melt processability of biopolymers that are not traditionally melt processable.

A plasticizer may be a low molecular weight non-volatile compound. Additional exemplary plasticizers include, but are not limited to, citric acid, triphenyl phosphate, camphor oil, amylacetate, allyurea, citrate esters, phthalic acid esters, dioctyl phthalate, fatty acid esters, benzoates, tartrates, chlorinated hydrocarbons, esters of adipic acid, polyols (e.g., glycerol, ethylene glycol (EG), diethylene glycol (DEG), triethylene glycol (TEG), tetraethylene glycol, polyethylene glycol, propylene glycol (PG), sorbitol, mannitol, xylitol, fatty acids, and/or vegetable oils), lecithin, waxes, amino acids, surfactants, and/or water.

In some embodiments, citric acid is present in a homogeneous reaction blend and it may function as both a charge-modifying agent and a plasticizer.

A catalyst may optionally be present in a homogeneous reaction blend. In some embodiments, a catalyst and/or a plasticizer may be combined with a biopolymer and at least one charge-modifying agent to form a homogenous reaction blend. A catalyst may be present in a homogeneous reaction blend in an amount of about 1% to about 100% or more by weight of a biopolymer present in the homogeneous reaction blend. In some embodiments, a catalyst may be present in a homogeneous reaction blend in an amount of about 1%, 5%, 10%, 20%, 30%, 40%, 50%, 60%, 70%, 80%, 90%, 100%, or more by weight of a biopolymer present in the homogeneous reaction blend.

A catalyst may accelerate the charge-modification and/or cross-linking reaction. In some embodiments, a catalyst may adjust the pH to enhance the opening of chemical bonds. Exemplary catalysts include, but are not limited to, sodium hypophosphite, sodium bisulfate, sodium bisulfite, and/or caustics (e.g., sodium hydroxide, calcium hydroxide, etc.). In some embodiments, a method of the present invention may be carried out at a pH of about 2, 3, 4, 5, 6, 7, 8, 9, 10, 11, or 12. In some embodiments, a method of the present invention may be carried out at a pH in a range of about 9 to about 12, about 10 to about 12, about 2 to about 7, or about 2 to about 5.

In some embodiments, the catalyst may be an initiator. In some embodiments, the cross-linking step may comprise reacting the biopolymer with at least one cross-linking agent, optionally in the presence of an initiator. The biopolymer may be a charge-modified biopolymer. Exemplary initiators include, but are not limited to, peroxides such as acyl peroxides (e.g., benzoyl peroxide) and dialkyl or aralkyl peroxides (e.g., di-t-butyl peroxide, dicumyl peroxide, cumyl butyl peroxide, 1,1-di-t-butylperoxy-3,5,5-trimethylcyclohexane, 2,5-dimethyl-2,5-di-t-butylperoxy hexane, and bis(t-butylperoxyisopropyl)benzene); ketone peroxides (e.g., cyclohexanone peroxide and methylethylketone peroxide); sodium methoxide, potassium persulfate, ceric ammonium, sodium hydroxide, and/or azo compounds (e.g., azobisisobutyronitrile).

An initiator may be present in a homogeneous reaction blend in an amount of about 1% to about 100% or more by weight of a biopolymer present in the homogeneous reaction blend. In some embodiments, an initiator may be present in a homogeneous reaction blend in an amount of about 1%, 5%, 10%, 20%, 30%, 40%, 50%, 60%, 70%, 80%, 90%, 100%, or more by weight of a biopolymer present in the homogeneous reaction blend.

Optional additives may be used in a method of preparing a modified biopolymer. Exemplary optional additives include, but are not limited to, dyes, pigments, organic fillers, inorganic fillers, softening agents (e.g., mineral oils and synthetic oils), flame retardants, crystallization accelerators, stabilizers (e.g., heat and light stabilizers), tie-agents, nucleating agents, other polymers (e.g., non-biopolymers), and/or the like.

Forming a homogenous reaction blend may comprise melt blending at least one biopolymer and at least one charge-modifying agent, optionally with at least one plasticizer, a catalyst (e.g., an initiator), and/or optional additives. In some embodiments, at least one biopolymer, at least one charge-modifying agent, at least one plasticizer, and optionally a catalyst may be combined to form a homogeneous reaction blend. In some embodiments, a homogeneous reaction blend may be formed and/or prepared using a reactive extrusion process. The reactive extrusion process may be carried out in an extruder.

In certain embodiments, a homogeneous reaction blend may be formed comprising at least two different biopolymers. In some embodiments, a homogeneous reaction blend may be formed comprising a charge-modified biopolymer and at least one different biopolymer, which may optionally be charge-modified. When two biopolymers are present in a homogeneous reaction blend, a first biopolymer may be present in the homogeneous reaction blend in an amount of about 10% to about 200% or more by weight of a second biopolymer present in the homogeneous reaction blend. In some embodiments, a first biopolymer may be present in a homogeneous reaction blend in an amount of about 10%, 20%, 30%, 40%, 50%, 60%, 70%, 80%, 90%, 100%, 110%, 120%, 130%, 140%, 150%, 160%, 170%, 180%, 190%, 200%, or more by weight of a second biopolymer present in the homogeneous reaction blend.

In some embodiments, a first biopolymer and a second biopolymer may be present in a homogeneous reaction blend in a ratio in a range of 0.1:1 to 4:1 (first biopolymer:second biopolymer), such as, for example, in a ratio in a range of 0.5:1 to 2:1 or 1:1 to 3:1. In certain embodiments, a first biopolymer and a second biopolymer may be present in a homogeneous reaction blend in a ratio of about 0.5:1, 1:1, or 1:0.5.

In some embodiments, the reacting and/or cross-linking step(s) may be carried out and/or performed in a homogeneous reaction blend. The reacting and/or cross-linking step(s) may be carried out and/or performed using a reactive extrusion process. In some embodiments, the reacting and/or cross-linking step(s) may be carried out at a temperature in a range of about 80° C. to about 200° C., such as, for example, at a temperature in a range of about 80° C. to about 120° C., about 80° C. to about 150° C., about 90° C. to about 120° C., about 100° C. to about 120° C., about 100° C. to about 200° C., about 150° C. to about 180° C., or about 110° C. to about 130° C. In certain embodiments, the reacting and/or cross-linking step(s) may be carried out at a temperature of about 90, 91, 92, 93, 94, 95, 96, 97, 98, 99, 100, 101, 102, 103, 104, 105, 106, 107, 108, 109, 110, 111, 112, 113, 114, 115, 116, 117, 118, 119, 120, 121, 122, 123, 124, 125, 126, 127, 128, 129, 130, 131, 132, 133, 134, 135, 136, 137, 138, 139, 140, 141, 142, 143, 144, 145, 146, 147, 148, 149, or 150° C. In some embodiments, the reacting and/or cross-linking step(s) may be carried out at a temperature of about 140° C. or less.

In some embodiments, the reacting and/or cross-linking step(s) may be carried out at a temperature that avoids degradation of a biopolymer and/or modified biopolymer. In some embodiments, increasing the temperature of the reacting and/or cross-linking steps may provide for an increased amount of charge-modification on the biopolymer if the temperature remains below the degradation temperature for the biopolymer. In some embodiments, the reacting step may be carried out and/or performed at a temperature in a range of about 100° C. to about 175° C., such as, for example, about 120° C. to about 140° C. or about 100° C. to 150° C. In some embodiments, the cross-linking steps may be carried out and/or performed at a temperature in a range of about 120° C. or more, such as, for example, about 120° C. to about 175° C. or about 120° C. to about 140° C.

One or more process conditions for a method of the present invention may be modified to provide a particular modified biopolymer, such as, for example, a super absorbent, ion exchange resin, etc., and/or a particular property of a modified biopolymer, such as, for example, the degree of charge modification, cross-linking, etc. Example processing conditions for a method of the present invention include, but are not limited to, the type of extruder (e.g., single screw vs. twin screw); screw diameter (D); screw length (L) (L/D may be used to describe an extruder configuration); screw configuration (i.e., specific types of shear inducing sections within an extruder which may range from gentle conveying elements to more shear intensive elements that may be designed to enhance uniform mixing within the extruder and/or accelerate a chemical reaction); temperature (overall and profile along various extruder zones); screw RPM; number of separate extruder zones where both temperature can be changed independent of other zones and different ingredients of the formulation can be added; and feed rate of different formulation elements into different zones. In some embodiments, the combination of one or more independently controlled process variables may influence dependent variables of residence time, mechanical energy input (SME) and/or shear. Changes in screw RPM may induce changes in shear, heating and/or residence time in the extruder.

In some embodiments, the reacting and/or cross-linking step(s) may be carried out in an extruder. The reacting and/or cross-linking step(s) may carried out in an extruder with a residence time in a range of about 0.1 minutes to about 30 minutes, such as, for example, in a range of about 0.1 minutes to about 10 minutes, about 0.5 minutes to about 5 minutes, about 1 minute to about 10 minutes, about 1 minute to about 5 minutes, or about 1 minute to about 3 minutes. In certain embodiments, the reacting and/or cross-linking step(s) may be carried out in an extruder with a residence time of about 0.1, 0.2, 0.3, 0.4, 0.5, 0.6, 0.7, 0.8, 0.9, 1, 2, 3, 4, 5, 6, 7, 8, 9, 10, 11, 12, 13, 14, 15, 16, 17, 18, 19, 20, 21, 22, 23, 24, 25, 26, 27, 28, 29, or 30 minutes. In some embodiments, the reacting and/or cross-linking step(s) may be carried out in an extruder with a residence time of about 5 minutes. In some embodiments, increasing the residence time of the reacting and/or cross-linking steps may provide for an increased amount of charge-modification on the biopolymer.

The reacting and/or cross-linking step(s) may carried out in an extruder having a screw RPM in a range of about 10 to about 500 rpm, such as, but not limited to, about 10 to about 200, about 50 to about 200, about 100 to about 200, about 125 to 250, about 100 to about 500, or about 90 to about 130. In certain embodiments, the reacting and/or cross-linking step(s) may be carried out in an extruder having a screw RPM in a range of about 40, 50, 60, 70, 80, 90, 100, 110, 120, 130, 140, 150, 160, 170, 180, 190, 200, 210, 220, 230, 240, 250, 260, 270, 280, 290, 300, 310, 320, 330, 340, 350, 360, 370, 380, 390, 400, 410, 420, 430, 440, 450, 460, 470, 480, 490, or 500 rpm. In some embodiments, the reacting and/or cross-linking step(s) may be carried out in an extruder having a screw RPM of about 120 rpm.

In some embodiments, the reacting and/or cross-linking step(s) may be carried out in an extruder with a Specific Mechanical Energy (SME) value of at least about 20 kJ/kg. In certain embodiments, the reacting and/or cross-linking step(s) may be carried out in an extruder with a SME value in a range of about 20 kJ/kg to about 500 kJ/kg or about 25 kJ/kg to about 250 kJ/kg. The SME value may be measured using methods known to those of skill in the art.

The step of reacting a biopolymer with a charge-modifying agent and the step of cross-linking the biopolymer may occur simultaneously. Alternatively or in addition, in some embodiments, the step of reacting the biopolymer with the charge-modifying agent and the step of cross-linking the biopolymer may be done sequentially. Thus, in some embodiments, the step of reacting the biopolymer with the charge-modifying agent may be carried out first to form a charge-modified biopolymer and then cross-linking step may be carried out with the charge-modified biopolymer.

Exemplary devices for carrying out a method of the present invention include, but are not limited to, co-rotational and counter rotational twin screws, thermal kinetic compounders, high shear mixers, paddle mixers, static mixers blenders, open-type mixing roll, closed Banbury mixer, kneader, single-screw extruder, vented screw extruder, and/or twin-screw extruder (e.g., a parallel or conical twin-screw extruder). In some embodiments, an extruder is used to carry out a method of the present invention. Exemplary screw configurations include those illustrated in FIG. 6. A low shear screw configuration may include a low number or no shear inducing elements or zones along the screw profile where shear inducing elements or zones may include mixing, kneading, and/or reversing elements or zones which increase the torque or load on the extrusion motor for a given mass flow rate. A medium and/or high shear screw configuration may include an increased number of shear inducing elements or zones compared to a low shear screw configuration.

In some embodiments, the components or reactants for one or more steps in a method of the present invention may be dry mixed together prior addition to an extruder. Alternately or in addition, two or more feeders (e.g., loss-in-weight feeders) may be used that supply the components or reactants to be blended to an extruder. In certain embodiments, multiple extruders may be used to feed melts of the blend components, such as in co-extrusion. In some embodiments, one or more components or reactants may be added to an extruder in powder form. The components and/or mixture blends may be sized by conventional means such as pelletization, granulation, and/or grinding.

A method of the present invention may be performed and/or carried out as a single-stage direct extrusion process or a multi-stage extrusion process. In some embodiments, the method comprises in-line compounding. In some embodiments, the method is carried out in an extruder comprising at least two reaction zones and the at least two reaction zones are used for one or more steps in the method for preparing a modified biopolymer of the present invention (e.g., a cross-linked, charge-modified biopolymer). For example, a method of the present invention may comprise reacting a biopolymer and at least one charge-modifying agent at a first reaction zone to form a charge-modified biopolymer and cross-linking the charge-modified biopolymer at a second reaction zone to form a cross-linked, charge-modified biopolymer.

In some embodiments, one or more reagents may be in powder form when added to an extruder and may not be in the form of a liquid or paste. In some embodiments, the one or more reagents in powder form may have a moisture content of about 20% by weight or less. Some embodiments include adding a biopolymer and/or charged-biopolymer to an extruder in powder form and/or adding one or more additional reagents (e.g., a charge-modifier, plasticizer, cross-linker, etc.) to the extruder in powder form. The one or more additional reagents may be added in the same or a different reaction zone than the biopolymer and/or charged-biopolymer.

In some embodiments, an extruder is used as one complete reaction vessel, which may allow for the reaction to occur along the entire length of the extruder. When two or more reaction zones are provided, the one or more process conditions (e.g., temperature, shear, etc.) in one or more reaction zones may be independently provided and/or changed. Some embodiments may include providing a different temperature and/or screw element in at least one reaction zone compared to another reaction zone. For example, in some embodiments, a mixture of a biopolymer (e.g., starch), plasticizer, charge-modifying agent, and catalyst may be introduced into a feed zone in an extruder and in the extruder the mixture may form a homogenous reaction blend. The reaction taking place in the extruder may be modified (e.g., accelerated and/or slowed) by varying the temperature in one or more reaction zones in the extruder. In some embodiments, the reaction may be accelerated by increasing the temperature in one or more reaction zones in the extruder. Some embodiments may include introducing shear in one more reaction zones, such as, e.g., zone 3 and/or zone 5 of an extruder, by having intense mixing elements in the screw to facilitate mixing and/or shear induced reaction. In some embodiments, the length of different reaction zones and/or the length of the extruder itself (e.g., by moving the injection zone closer to the end of the extruder) may be varied or adjusted, such variations or adjustments may modify the degree of reaction. The length of the extruder is generally defined as the length over diameter ratio or L/D.

In some embodiments, an extruder may be used as a sequential reactor. For example, in some embodiments, a mixture of a biopolymer (e.g., starch), plasticizer, and charge-modifying agent may be introduced into a feed zone of an extruder. The mixture may be heated as it is transported through one or more reaction zones (e.g., one or more initial reaction zones, such as, e.g., zones 1 and 2) using conveying elements on the screw, and the charge-modifying agent may react with the biopolymer to form a charge-modified biopolymer. Then, a cross-linking agent may be added in either solid or liquid form into one or more reaction zones (e.g., zone 3) to form the cross-linked, charge-modified biopolymer. In some embodiments, following the reaction zone(s) in which the charge-modifying agent was added, an intense mixing screw element may be placed on the screw in one or more reaction zones (e.g., in zone 4 and/or 5) to mix the cross-linking agent with the charge-modified biopolymer. The cross-linking reaction may be facilitated by different temperatures and/or different screw elements in one or more reaction zones (e.g., zone 4 and/or 5). In some embodiments, a foaming agent (e.g., water) may be injected into an extruder (e.g., in a reaction zone near the end of the extruder, such as, e.g., at zone 6), which may cause the cross-linked, charge-modified biopolymer to expand as it exits the die. Some embodiments include that the biopolymer introduced into a feed zone of an extruder is in powder form.

In some embodiments, a method of the present invention may comprise foaming a modified biopolymer of the present invention (e.g., a cross-linked, charge-modified biopolymer). Foaming may be done to induce porosity and/or void size of the modified biopolymer, such as by opening and/or increasing cell porosity. Foaming may aid in increasing fluid, charged species, and/or metal sequestration, binding, absorption, chelation, uptake and/or the like. In some embodiments, the modified biopolymer may have open, connected pores, which may facilitate mass transfer within the modified biopolymer and access of ions in a fluid to the ionic binding sites of the modified biopolymer. Foaming the modified biopolymer may modify (e.g., increase or decrease) the viscoelastic properties of the modified biopolymer. In some embodiments, the amount or degree of the modification may vary with the amount of a fluid (e.g., water, carbon dioxide, nitrogen, etc.) absorbed in the modified biopolymer at the time of foaming.

A foaming agent may be a chemical agent or physical agent. Exemplary foaming agents, include, but not are limited to, supercritical nitrogen (N₂) calcium carbonate (CaCO₃), water (e.g., steam), and/or supercritical carbon dioxide (CO₂).

In some embodiments, a method of the present invention may comprise treating a modified biopolymer of the present invention (i.e., a post-treatment), such as, for example, thermally treating a charge-modified biopolymer and/or cross-linked, charge-modified biopolymer post extrusion. A post-treatment of the prevent invention may increase the degree of cross-linking present in a modified biopolymer of the present invention and/or may increase and/or improve charge density and/or charge modification of a modified biopolymer. In some embodiments, a post-treatment of the present invention may decrease the soluble gel fraction in a modified biopolymer. The modified biopolymer in solid form may be undergo a post-treatment. In some embodiments, a post-treatment of the present invention may fine tune and/or modify the properties of a modified biopolymer of the present invention.

A post-treatment may comprise heating the modified biopolymer. In some embodiments, a method of the present invention may comprise heating the modified biopolymer at a temperature in a range of about 80° C. to about 180° C., such as, for example, about 100° C. to about 150° C. or about 120° C. to about 140° C., for a period of time in a range of about 0.5 minutes to about 24 hours, such as, for example, about 5 minutes to about 180 minutes, or about 30 minutes to about 90 minutes. In some embodiments, a post-treatment may comprise heating the modified biopolymer at a temperature of about 110° C. to about 130° C. for a period of time in a range of about 60 minutes to about 120 minutes. In some embodiments, a post-treatment may comprise heating the modified biopolymer at a temperature of about 130° C. to about 150° C. for a period of time in a range of about 10 minutes to about 50 minutes.

In some embodiments, a method of the present invention may comprise removing unreacted reagents, soluble and/or low molecular weight species, and/or degradation products from a modified biopolymer of the present invention, such as, for example, by rinsing, dialyzing, and/or the like the modified biopolymer. Some embodiments include removing unreacted reagants from the modified biopolymer after a post-treatment. Some embodiments of the present invention may include drying the modified biopolymer (e.g., drying at a temperature of about 40° C.). In some embodiments, a method of the present invention may comprise sizing the modified biopolymer by conventional means, such as, for example, pelletization, granulation, milling, and/or grinding.

According to some embodiments of the present invention, a method of the present invention may comprise forming a homogeneous reaction blend comprising a starch, at least one charge-modifying agent, optionally at least one plasticizer, and optionally a catalyst, and reacting the starch and the at least one charge-modifying agent to form a charged-modified starch. In some embodiments, the at least one charge-modifying agent may be an acid such as, for example, citric acid, the optional at least one plasticizer may be water and/or glycerol, and/or the optional catalyst may be sodium hypophosphite. The reacting step may comprises reacting starch and the charge-modifying agent (e.g., citric acid) in a ratio in a range of 0.1:1 to 4:1 (charge-modifying agent:starch), such as, for example, in a ratio in a range of 0.5:1 to 2:1 or 1:1 to 3:1.

The charge-modified starch may be cross-linked with another biopolymer, such as, for example chitosan to form a cross-linked, charge-modified starch-chitosan. In some embodiments, the chitosan is charged modified, such as, but not limited, protonated. In certain embodiments, the method may comprise combining charged-modified starch with chitosan, at least one plasticizer, and optionally a charge-modifying agent, and cross-linking the charged-modified starch and chitosan. In some embodiments, a charge-modifying agent may be an acid (e.g., acetic acid, such as glacial or concentrated acetic acid) and may react with the chitosan to form charge-modified chitosan that may be cross-linked with the charge-modified starch. In some embodiments, charge-modified chitosan may be prepared by reacting chitosan and acetic acid in an amount of about 1% to about 40%, such as, for example, about 2.5% to about 13% or about 20% to about 40% by weight of the chitosan, wherein acetic acid is added directly to the chitosan without the presence of water.

A method of preparing a cross-linked, charge-modified starch-chitosan may comprise providing in an extruder starch in an amount in a range of about 5 wt % to about 50 wt % and chitosan in an amount in a range of about 5 wt % to about 50 wt % to form a homogeneous reaction blend. In some embodiments, the chitosan may be charge-modified chitosan. The homogeneous reaction blend may further comprise a charge-modifying agent (e.g., citric acid) in an amount in a range of about 5 wt % to about 40 wt %, a catalyst in an amount in a range of about 0.1 wt % to about 5 wt %, and a plasticizer in an amount in a range of about 20 wt % to about 40 wt %.

According to some embodiments, a method of the present invention may comprise combining starch, chitosan, at least one charge-modifying agent, a catalyst, and a plasticizer to form a homogenous reaction blend; charge-modifying the starch and chitosan to form a charge-modified starch and a charge-modified chitosan; and cross-linking the charge-modified starch and charge-modified chitosan to form a cross-linked, charge-modified starch-chitosan. In some embodiments, the combining step may be carried out by providing, adding, feeding, injecting and/or the like all components into the extruder at substantially the same time. This may allow for the charge-modifying and cross-linking reactions to occur simultaneously.

In some embodiments, a method of the present invention may comprise combining starch, a first charge-modifying agent, and a catalyst to form a homogeneous reaction blend comprising a charge-modified starch; adding chitosan, a plasticizer, and optionally a second charge-modifying agent to the homogeneous composition comprising the charge-modified starch; and cross-linking the charge-modified starch and chitosan to form a cross-linked, charge-modified starch-chitosan. The chitosan, in some embodiments, may be charged-modified and/or added to an extruder in the presence of a charge-modifying agent, such as, for example, glacial acetic acid. In some embodiments, the method may use multiple inlets of an extruder. For example, starch, the first charge-modifying agent, and the catalyst may be added at a first inlet and/or reaction zone in an extruder, and chitosan, the plasticizer, and optionally the second charge-modifying agent may be added at a second inlet and/or reaction zone in an extruder. This may allow for the charge-modifying and cross-linking reactions to occur simultaneously and/or sequentially.

In certain embodiments, a method of the present invention may comprise combining starch, a first charge-modifying agent, and a catalyst to form a charge-modified starch; forming a homogeneous reaction blend comprising the charged-modified starch, chitosan, a plasticizer, and optionally a second charge-modifying agent; and cross-linking the charge-modified starch and chitosan to form a cross-linked, charge-modified starch-chitosan. This may allow for the charge-modifying and cross-linking reactions to occur sequentially. The chitosan, in some embodiments, may be charged-modified and/or added to an extruder in the presence of a charge-modifying agent, such as, for example, glacial acetic acid.

In some embodiments, the charge-modified starch is prepared and/or formed by forming a homogeneous reaction blend in an extruder. The charge-modified starch may be extruded and the extrudate may optionally be ground into a powder and/or pelletized. The extrudate may then be combined with chitosan, a plasticizer, and optionally a second charge-modifying agent to form a homogeneous reaction blend.

A method of the present invention may provide a formed modified biopolymer (e.g., a cross-linked, charge-modified biopolymer). In some embodiments, the method may comprise grinding, milling, pelletizing, drawing, compressing, shaping, and/or the like to provide a formed modified biopolymer of the present invention. The formed product may be of any shape and/or size. In some embodiments, a method of the present invention provides a plurality of formed products of substantially uniform size and/or shape (e.g., varying in size and/or shape by less than about 20%). In some embodiments, a method of the present invention provides a variety of particle sizes and/or shapes. In some embodiments, a method of the present invention may provide a modified biopolymer (e.g., a cross-linked, charge-modified biopolymer) that is in the form of a bead, column, sheet, powder, particle (e.g., nanoparticles, microparticles, etc.), ribbon, fiber, film, pellet, and/or the like. In some embodiments, a method of the present invention may provide a modified biopolymer in the form of a particle having a diameter in a range of about 1 micron to 2,000 microns, such as, but not limited to, in a range of about 10 microns to about 1000 microns, about 100 microns to about 1000 microns or about 300 to about 800 microns. In some embodiments, a modified biopolymer of the present invention (e.g., a cross-linked, charge-modified biopolymer) having a particle size in a range of about 300 to about 800 microns or less than about 500 microns may be suitable for use as an absorbent. In some embodiments, a modified biopolymer of the present invention (e.g., a cross-linked, charge-modified biopolymer) having a particle size in a range of about 10 to about 150 microns or less than about 100 microns may be suitable for use as an ion exchange material.

In some embodiments, a modified biopolymer of the present invention (e.g., a cross-linked, charge-modified biopolymer) may be used as and/or to prepare a consumer product, such as, but not limited to, a diaper, hygiene product, and/or wound dressing. In some embodiments, a modified biopolymer of the present invention (e.g., a cross-linked, charge-modified biopolymer) may be used as and/or to prepare an ion exchange resin and/or absorbent. Thus, in some embodiments, a modified biopolymer of the present invention may be an ion exchange resin, ion removal resin, metal chelating and/or adsorbing resin, and/or an absorbent including high performing absorbents, such as, for example, super absorbents. In some embodiments, a modified biopolymer of the present invention (e.g., a cross-linked, charge-modified biopolymer) may remove contaminants from a fluid and/or absorb a fluid.

Further exemplary industries and/or uses for a modified biopolymer of the present invention include, but are not limited to, water treatment such as, for example, single-use ion exchange for water deionization (e.g., for laboratories and/or electronics), potable water desalination, potable water contaminant and heavy metals adsorbents, and an alternative to activated carbon for dechlorination; hygienic super absorbent applications (SAP) such as, for example, baby diaper absorbents, adult incontinence absorbents, feminine hygiene absorbents; non-hygenic SAP applications such as, for example, sub-sea cable wraps, re-usable gel/ice packs, liquid waste solidification, pet pads, meat pads, concrete additives, remove water from oil and/or hydrocarbons, liquid/solid separation, waste lagoon remediation, paint solidification, agricultural and horticultural soil amendments, mortuary absorbents, whole blood or blood mixture absorbents, medical waste solidification and spill control, drug delivery systems, and wound dressings; energy such as, for example, hydraulic fracturing flowback water treatment or reuse, guar alternative hydraulic fracturing viscosifying agent, hydraulic fracturing friction reducer additive, lost circulation drilling fluid additive, oil refinery water treatment, cooling tower water softening, boiler feed water deionization, coal ash and flu vent remediation, and nuclear isotope removal; mining such as, for example, metals mining water treatment, metal removal from mining solutions, and coal mining water treatment; environmental such as, for example, pump and treat water remediation, in situ reactive barrier remediation, and sludge absorption and dewatering; packaging such as, for example, biobased packaging films and biobased structural packaging; paper such as, for example, pulp and paper strength additives and/or coatings for paper; textiles such as, for example, textile adhesives, starch ester alternative for textile manufacture, and textile non-woven thickening agents; and/or construction such as, for example, construction adhesive in wallboard. In some embodiments, a modified biopolymer of the present invention may be useful in the paper industry, cosmetics, tissue engineering, hydrogels, drug delivery applications, photonics applications, and/or as a flocculant and/or coagulant.

The present invention is explained in greater detail in the following non-limiting Examples.

EXAMPLES Example 1.1—Extruded Charge Modified Biopolymer (Example of Citric Acid Grafted on to Starch at ˜2mm Scale)

A twin screw conical extruder manufactured by DSM, a parallel twin screw extruder manufactured by Leistritz, and a parallel twin screw extruder manufactured by Wegner were used to prepare charge-modified starch. The extruder properties are provided in Table 1. Various extruders listed here allow for demonstration of scalability from lab scale to production-relevant scale. Furthermore, multiple extruders allow for transposition of process parameters across a range of extruder configurations and size.

Additionally, the parallel twin screw extruders manufactured by Lestritz and Wegner supported multiple reactions zones, allowing for increased capabilities, including: temperature, screw, and injection profiles. Examples of temperature and injection profiles may be found in Examples 1.2, 5.1, and 7, below.

TABLE 1 Extruder properties for a range of extruder configurations and sizes Extruder Manufacturer DSM Thermo Fisher Leistritz Wegner Extruder Model Xplore Process 11 N/A TX-52 Residence Time 0.25-10 mins 0.25-5 mins ~3 mins ~3 mins Screw Size (Screw Diameter) 3 cm 11 mm 18 mm 52 mm L/D 5 40  40 27 Die Size 1-2 mm 0.5-11 mm 1 mm & 4.5 mm 2-4 mm Rotation Corotating Co-rotating Corotating Corotating Screws Screws Screws Screws Throughput 0.05-0.2 Kg/hr 0.1-5 Kg/hr 0.5-8 Kg/hr 3-30 Kg/hr Type of heating Electric Electric Electric Electric Number of heating zones 1 8  8  1 Type of Die Single Single single holes 1 or 2 holes hole/circular hole/circular Additive zones One 8 3 feed ports 2 feed ports, 1 extra for foaming agent Type of cooling Water Water Air Water

In preparing the charge-modified starch, the following parameters were varied: temperature, screw RPM, and amount of citric acid using each extruder. Table 2 sets forth the ranges for the temperature, screw RPM, and amount of citric acid tested using each extruder.

TABLE 2 Parameter ranges for charge-modified starch for each extruder. Range Range Range Parameter (DSM) (Leistritz) (Wegner) Temperature Ranges (° C.) 90-150 100-120 100-125 RPM Ranges (RPM) 60-200 120-200 120-200 Citric Acid Ranges (rel 50-100  50-100  50-100 % to starch)

Starch (Native Corn Starch, Item 18321, Batory Foods, Des Plaines Ill.), citric acid (Item 756707, Univar, Downers Grove, Ill.) as a charge modifier and plasticizer, and sodium hypophosphate (SHP) (Item S1320, Spectrum Chemical, New Brunswick, N.J.) as a catalyst were combined and hand mixed in powder form. Powder mixtures were loaded into custom powder injectors and input into the extruder feed port. Various amounts of citric acid were added to the mixture as provided in Table 2. The resulting mixture was added to the extruder as a powder at varying extrusion conditions as provided in Table 2. The powder mixture was melt-blended in the extruder to form a homogeneous blend reaction in which the citric acid was grafted onto the starch to form a charge-modified starch, termed starch citrate. In some runs, this charge-modified starch was utilized as a precursor polymer to subsequently cross-link to another biopolymer as described in Example 5. Select samples underwent a thermal post treatment following extrusion by way of vacuum oven at 120° C. for 90 mins.

Table 3 provides specific parameters tested on the DSM extruder with responses described in Table 4 and described below. Each sample was titrated to determine its charge density, and analyzed via FTIR (at wavelengths of 1720 cm⁻¹) to determine each sample's relative carboxyl content via methods described below. Additionally, parameters such as DI uptake, and % extractables were measured as qualitative gauges of material performance.

TABLE 3 Process parameters for preparing charged-modified starch on a DSM extruder Sample # Sample 1.1A Sample 1.1B Sample 1.1C Sample 1.1D Sample 1.1E Temperature (° C.) 140 140 100 140 125 RPM 120 120 120 120 120 Post Treatment Yes No Yes Yes Yes Citric Acid (wt % 150 150 50 50 75 relative to Starch) SHP (wt % relative  20  20 20 20 20 to Citric Acid)

Fourier Transform Infrared Spectroscopy (FTIR) is a measure of a samples' absorbance/transmittance of wavelengths in the IR spectrum. The intensity of absorbed IR radiation at a given wavelength can be correlated to particular covalent bonds. When data is normalized to the primary alcohol peak (˜1000 cm⁻¹), relative peak intensities may be used to estimate the amount characteristic groups on the polymer, where decreasing transmittance or, inversely, increasing absorbance indicates an increased degree of reagent grafting. Bonds of interest for biopolymers modified with citric acid, such as, for example, starch citrate, include the carboxyl (R—CO2H) bond at ˜1713 cm⁻¹,where decreasing transmittance or, inversely, increasing absorbance indicates an increased degree of charge density.

Back titration is a measure of charge density in anionic, charge-modified biopolymer samples. The results of this measurement technique scales with the FTIR data. As described here in Example 1.1, along with Examples 1.2, 1.3, 2.1. 3.1, 3.2, and 3.3, 0.2-0.3 g of sample was exposed to 50 ml of 0.05 M NaOH solution for 1 hr. One drop of phenolphthalein (Item 3241N80, Thomas Scientific, Swedesboro, N.J.) was added and mixed into solution to act as a visual indication, approximating neutrality of the solution. A pH probe was used to monitor acid/alkaline nature of the solution during mixing and titration. The solution was then titrated with 0.05M HCl at, ˜0.05 ml/second. The volume of HCl required to reach pH neutrality was recorded and assumed to be equivalent to the number of mols needed to neutralize excess NaOH in solution. The difference between the recorded mols and initial mols was then normalized to the original sample weight to yield a mol/g or mol/g charge density unit.

DI uptake is a measure of a sample's degree of swelling (i.e., its absorbency by weight under given conditions). DI uptake was measured by inserting ˜0.25 g sample/cm in 33 mm diameter, of 12-14 kD dialysis tubing (Item 684219, Carolina Biological, Burlington, N.C.). The ends of tubing were sealed and labeled, then exposed to 20 ml DI water per gram of sample for 72 hours. DI water was replaced every 2-3 hours over the course of a 72 hr period. Samples were then removed from the dialysis tubing and weighed. Changes in weight between the initial and final (wet) measurements were normalized to initial mass to grams of DI water absorbed per gram of sample (g/g).

Samples were then dried using a forced air oven and/or freeze dryer. Weight loss between dried sample and initial sample weight (pre dialysis) was used to calculate extractables as a % of initial sample (inverse of yield). These extractables reflect a measure of the amount of sample that elutes upon initial contact with water. This parameter qualitatively measures the mass fraction of unreacted moieties, plasticizer, and/or degraded polymeric products in a given sample.

TABLE 4 Properties of the charged-modified starch. FTIR Titration DI Uptake Extractables Sample # (% Trans.) (meq/g) (g/g) (%) 1.1A 36 5.9 3.4 89 1.1B 96 1.9 2.8 87 1.1C 59 2.8 2.7 37 1.1D 48 4.2 3.1 30 1.1E 49 3.8 5.4 49

As can be seen from Tables 3 and 4, charge-modified starch was produced in the process example of reactive extrusion described here. % Transmittance as measured via FTIR is shown to decrease significantly below that of starch (94.5%) while titration values are shown to increase significantly over that of starch (0 meq/g).

Temperature and citric acid (charge modifying agent) concentration are the parameters where increasing inputs show increased charge density. Furthermore, inclusion of a thermal post treatment after extrusion was also studied and addition of a post treatment also shows increasing charge density. Relative similarity and relatively low values of DI uptake parameters across indicate a lack of crosslinking. Extractable values are indicative of excess reagent and generally trend with charge modifier concentration. FTIR transmittance values achieved ranged from approximately 35-98% while charge density values achieved ranged from approximately 1 to 6.5 meq/g.

Example 1.2—Extruded Charge Modified Biopolymer (Example of Citric Acid Grafted on to Starch at 18 mm Scale)

A parallel twin screw extruder with multiple injection and reaction zones manufactured by Leistritz was also used to prepare charge-modified starch citrate. These experiments were performed to determine scalability and behavior of materials through varied reaction zones. The extruder properties are provided in Table 1 above. FIG. 2 illustrates the 8-zone extruder with injection ports in this configuration located prior to zone 1 and at zone 3.

Raw materials were prepared in a similar manner to extrusion as described above in Example 1.1. However, samples were mixed in 1 kg units and fed using gravimetric powder feeders manufactured by Brabender (Duisburg, Germany) to account for scale. Studies below utilized multiple injection and reaction zones to simulate full-scale extrusion processes. Screw profile utilized is described in FIG. 6 (medium shear screw). Powder samples of each of the following components: starch, citric acid, and SHP were fed into the primary injection zone (prior to zone 1) where the mixture was allowed to react at 120° C. Without wishing to be bound to any particular theory, at this temperature the citric acid dehydrates to yield an anhydride that reacts faster with the free hydroxyl groups. Temperature profiles for each zone are detailed in Table 5 below. Extrusion and composition parameters for starch citrate were varied as described in Table 6 below. In some runs, extruded samples in solid form were post-treated by placing the charge-modified starch in an oven at 120° C. for 90 minutes. Specific examples of process parameters and resulting responses are shown in Tables 7 & 8 below, respectively.

TABLE 5 Temperature and injection parameters for charge-modified starch via parallel twin- screw extruder. Zone 1 2 3 4 5 6 7 8 Temperature (° C.) 100 105 115 120 120 120 120 115 Injection Starch + N/A N/A N/A N/A N/A N/A N/A N/A Reagents

TABLE 6 Parameter ranges for charge-modified starch via 18 mm, parallel twin-screw extruder. Temperature Ranges (° C.) 100-120 (see Table 5) RPM Ranges (RPM) 120-200 Citric Acid Ranges (rel % to starch)  50-100

TABLE 7 Process parameters for preparing charged-modified starch via 18 mm, parallel twin-screw extruder. Sample # Sample 1.2A Sample 1.2B Sample 1.2C Sample 1.2D Temperature (° C.) 100-120 100-120 100-120 100-120 (multiple zones) (multiple zones) (multiple zones) (multiple zones) RPM 100 160  100  170  Post Treatment Yes Yes Yes Yes Citric Acid (wt % relative to Starch) 100 50 75 75 SHP (wt % relative to starch)  20 20 20 20

TABLE 8 Properties of the charged-modified starch. FTIR Titration DI Uptake Extractables Sample # (% Trans.) (meq/g) (g/g) (%) 1.2A 35 6.55 1.7 32 1.2B 53 2.10 1.1 10.5 1.2C 54 2.0 1.8 45 1.2D 43 5.8 1.3 10

As can be seen from Tables 7 and 8, this work demonstrated the feasibility of producing charge-modified starch via a reactive extrusion process. % Transmittance as measured via FTIR is shown to decrease significantly below that of starch (94.5%) while titration values are shown to increase significantly over that of starch (0 meq/g). Furthermore, it should be noted that titration and FTIR values have a positive correlation. While not wishing to be bound to any particular theory, it appears that increased RPM in this method can improve the degree of charge modification as a response to increased shear.

Example 1.3—Extruded Charge Modified Biopolymer (Example of Citric Acid Grafted on to Starch at 52 mm Scale)

A parallel twin screw extruder manufactured by Wegner was used to prepare charged-modified starch and to further demonstrate scaling. The extruder properties are provided in Table 1.1 above. Screw profile utilized largely conforms to a purely conveying screw as described in FIG. 6 (low shear screw).

Raw materials for charge-modified starch were prepared in a similar manner to the extrusion processes described above. However, samples were mixed and injected in ˜2 kg units to account for the larger scale and continuous nature of this extruder. Extrusion and composition parameters for starch citrate were varied as described in Table 9 below. Specific examples of process parameters and resulting responses are shown respectively in Tables 10 and 11 below, respectively. In some runs, extruded samples in solid form were post-treated by placing the charge-modified starch in an oven at 120° C. for 90 minutes.

TABLE 9 Parameter ranges for charge-modified starch via 52 mm, parallel twin-screw extruder. Temperature Ranges (° C.) 100-125 RPM Ranges (RPM) 120-200 Citric Acid Ranges (wt % relative  50-100 to starch)

TABLE 10 Process parameters for preparing charged-modified starch via 52 mm, parallel twin screw extruder. Sample # Sample 1.3A Sample 1.3B Temperature (° C.) 110 120 RPM 120 100 Post Treatment Yes Yes Citric Acid (wt % relative to 66 66 Starch) SHP (wt % relative to Citric Acid) 20 20

TABLE 11 Properties of the charged-modified starch. FTIR Titration DI Uptake Extractables Sample# (% Trans.) (meq/g) (g/g) (%) 1.3A 65 2.9 N/A 64 1.3B 69 2.4 N/A 68

This work demonstrated the feasibility of producing charge-modified starch via a reactive extrusion process. % Transmittance as measured via FTIR is shown to decrease significantly below that of starch (94.5%) while titration values are shown to increase significantly over that of starch (0 meq/g). Examples 1.1E, 1.2C and 1.3 are used to compare samples at similar processing conditions. It is concluded from the similar responses that parameters listed in these examples are transposable across a significant range of extruder sizes (representing from laboratory benchtop to commonly-used industrial sizes).

Example 2.1—Extruded Charge Modified Biopolymer (Examples of Additional Anionic Charge Modifiers Grafted on to Starch)

In addition to citric acid, additional anionic charge modifiers are demonstrated in the example below. Starch was charged modified using maleic anhydride (Item 63200-500G-F, Sigma-Aldrich, Mo., St. Louis) a catalyst (NaOH, Reagent ACS, Item 630, GFS Chemicals, Powell Ohio), and plasticizer to form an anionic starch. Table 12 sets forth the ranges for the temperature, screw rpm, and amount of reagent tested using a Process 11, 11 mm parallel twin screw extruder as described in Example 1.1, above. Screw profile utilized is described in FIG. 6 (medium shear screw). Specific examples of process parameters and resulting responses are shown in Tables 13 and 14 below, respectively. In some runs, extruded samples in solid form were post-treated by placing the charge-modified starch in an oven at 120° C. for 90 minutes.

In addition to charge density (measured via titration), solubility of each sample was also studied. Here, purified samples (as described in the dialysis process above) are used. 0.25 g of sample is mixed into in a beaker with 25 ml of DI water at 60C. Beaker with mixture is set stirring on hotplate and held at 60 C for 15 mins. Mixture is then centrifuged at 250 g (1800 RPM & 7 cm radius) for 20 mins to separate solid fraction from the liquid fraction, including dissolved solids. A pipette is then used to decant the liquid layer and discarded. Aluminum weigh pans stored in a desiccator and with predetermined weights are used to collect remaining solids. Weigh pans and solids are then dried in a forced air oven for 48 hrs at 40° C. Weigh pans and samples are removed from the forced air oven and immediately weighed. Sample weights as a fraction of initial weights are recorded as a % Solubility.

TABLE 12 Parameter ranges of the anionic-modified starch on an 11 mm, parallel twin screw extruder. Temperature Ranges (° C.) 85-140 RPM Ranges (RPM) 10-500 Maleic Anhydride Ranges (wt %  5-120 relative to starch) Catalyst (NaOH) Ranges (wt % 2-60 relative to starch Plasticizer Ranges (wt % relative Water, Glycerol, & to starch) Water/Glycerol mixes at 40%

TABLE 13 Process parameters for preparing anionic-modified starch via 11 mm, parallel twin screw extruder. Example 2.1A Example 2.1B Temperature (° C.) 110  110  RPM (RPM) 50 50 Post Treatment No No Maleic Anhydride Ranges (wt 30 60 % relative to starch) Catalyst (NaOH) Ranges (wt % 12 24 relative to starch Plasticizer (wt % relative to Water (40%) Water (40%) starch)

TABLE 14 Properties of the Anionic Modified Starch FTIR Titration Solubility Sample# (% Trans) (meq/g) (%) 2.1A 83 3.26 76 2.1B 73 5.11 84

Data indicated that a charge-modified starch was produced via a reactive extrusion process. % Transmittance as measured via FTIR is shown to decrease significantly below that of starch (94.5%) while titration and solubility values are shown to increase significantly over that of starch (0 meq/g and 7%, respectively). Ranges of charge density varied from 1.3-6.3 meq/g, and solubility varied from 27-86%. The level of charge modification of the starch increased with increasing reagent concentration. Data are further confirmed via increasing solubility with increasing charge density.

Example 2.2—Extruded Charge Modified Biopolymer (Examples of Cationic Charge Modifiers Grafted on to Starch)

In addition to anionc charges, starch was charge-modified to form a cationic starch. The cationic charge-modified starch was prepared by varying the following parameters: temperature, screw rpm, amount of charge modifying reagent (glycidyltrimethylammonium chloride [Sigma Aldrich Item 50053-1L]), catalyst (Sodium Hydroxide) and plasticizer content. Table 15 sets forth the ranges for the studied parameters in the Leistritz, 11 mm extruder.

TABLE 15 Parameter ranges of the anionic-modified starch on an 11 mm, parallel twin screw extruder. Temperature Ranges (° C.) 85-140 RPM Ranges (RPM) 10-500 glycidyltrimethylammonium chloride  5-150 Ranges (wt % relative to starch) Catalyst (NaOH) Ranges (wt % 2-60 relative to starch Plasticizer Ranges (wt % relative Water, Glycerol, & to starch) Water/Glycerol mixes at 40%

Starch powder was mixed with a catalyst (NaOH) in powder form. Plasticizer was then added to the mixture containing the starch and catalyst and mixed well by hand. The mixture was then input into the extruder.

Table 16 provides specific parameters tested with test responses described in Table 17. Note, temperature settings were set to apply a uniform temperature for all heating zones. Although temperature profiles were utilized in other experiments, they are not detailed here. Screw profile utilized is described in FIG. 6 (medium shear screw). Each sample was tested to determine its charge density (degree of substitution) via elemental analysis (measuring nitrogen).

Elemental analysis may be used to measure charge density for cationic charge-modified biopolymer samples, whereas titration may be used to measure charge density for anionic charge-modified biopolymer samples. Elemental analysis was carried out by means of Perkin Elmer 2400 CHNS Analyzer: The Perkin Elmer 2400 was used to determine total elemental carbon, nitrogen, hydrogen, or sulfur by total combustion. The Degree of Substitution (DS) was determined by nitrogen and calculated according to Equation (1) below:

DS=162.15×% N/1401−151.64×% N  (1),

where DS is the degree of substitution and % N is the measured nitrogen content. Furthermore, % N is nearly 0% but a non-zero number (e.g. 0.002). It is subtracted from all measurements for precision.

TABLE 16 Process and formulation parameters for preparing cationic charge-modified starch. Sample # Sample 2.2A Sample 2.2B Sample 2.2C Sample 2.2D Temperature (° C.) 90 120 90 90 Plasticizer (wt % relative to starch) Water (40%) Water (40%) Water (40%) Water (40%) RPM 100 120 50 50 Post Treatment No No No Yes glycidyltrimethylammonium 4 85 30 30 chloride (wt % relative to Starch) NaOH (wt % relative to Starch) 1.2 24 12 12

TABLE 17 Properties of the cationic charged-modified starch. Sample # Degree of Substitution* Solubility (%) 2.2A 0.035 28 2.2B 0.12 68 2.2C 0.19 76 2.2D 0.21 13 *Degree of substitution as measured by nitrogen content

Once again, a charge-modified starch was produced in this reactive extrusion process. Degree of substitution and solubility values were significantly greater than that of starch (0 DS, and 0.4% solubility, respectively) and demonstrate charge modification of a cationic starch via reactive extrusion. A range of DS values are produced. The DS values achieved here are significantly higher than previously reported values of DS for cationic starch produced via reactive extrusion.

In example 2.2D, inclusion of post treatment shows increased degree of substitution with simultaneous reduction in solubility indicating presence of cross linking as discussed in later examples.

Example 3.1—Extruded Charge Modified Biopolymer (Demonstration of Charge Grafting onto Hemicellulose)

In addition to starch, additional biopolymers were utilized to demonstrate charge modification. Hemicellulose (Xylan from Beechwood>=90%, Item X4252, Sigma Aldrich, St. Louis Mo.) was charge modified with citric acid to form an anionic hemicellulose using the DSM extruder described in Example 1.1. In preparing the charge-modified hemicellulose, the following parameters were varied: temperature, screw rpm, and amount of citric acid. Table 18 sets forth the ranges for the temperature, screw rpm, and amount of citric acid tested using the twin screw conical extruder.

TABLE 18 Parameter ranges for charge-modified hemicellulose via twin screw conical extruder. Temperature Ranges (° C.) 90-150 RPM Ranges (RPM) 50-200 Citric Acid Ranges (wt % relative 40-150 to hemicellulose)

Reagents in powder form were hand mixed in 50 g batches, loaded into the extruder using custom powder injectors, and fed into the extruder at feed rates determined to be relatively and qualitatively consistent. Table 19 provides specific parameters tested with test responses described in Table 20. The FTIR spectra for the charge-modified hemicellulose and for unmodified hemicellulose is provided in FIG. 3. Charge density values are reported according to the titration method described in Example 1.1. It should be noted that in this example, charge density values of the raw materials are measured and then subtracted from measured values to show a degree of change in charge density above that of the raw biopolymer.

TABLE 19 Process and formulation parameters for preparing charge-modified hemicellulose. Sample # Sample 3.1A Sample 3.1B Temperature (° C.) 140 140 RPM 120 120 Post Treatment No Yes Citric Acid (wt % relative to 150 150 Hemicellulose) SHP (wt % relative to Citric Acid)  20  20

TABLE 20 Properties of the charged-modified hemicellulose. Sample # FTIR (% Trans.) Titration (meq/g) 3.1A 81.4% 1.66 3.1B 53.4% 4.68

A charge-modified hemicellulose was produced via reactive extrusion. FTIR analysis shows % Transmission values significantly lower than that of unmodified hemicellulose (91%) and titration values significantly greater than that of unmodified hemicellulose (0 meq/g), indicating charge modification of the hemicellulose.

Example 3.2—Extruded Charge Modified Biopolymer (Demonstration of Charge Grafting onto Pectin)

Pectin (Item 76282, Sigma Aldrich, St. Louis, Mo.) was charge modified to increase the anionic property of pectin by grafting additional carboxylic acid groups onto pectin using the DSM extruder described in Example 1.1. Experimental methods followed those in Example 3.1. Table 21 sets forth the ranges for the temperature, screw rpm, and amount of citric acid tested using the twin screw conical extruder.

TABLE 21 Parameter ranges for charge-modified pectin via twin screw conical extruder. Temperature Ranges (° C.) 90-150 RPM Ranges (RPM) 50-200 Citric Acid Ranges (wt % relative 40-150 to pectin)

Table 22 provides specific parameters tested with test responses described in Table 23. If the sample underwent a post treatment, then the sample was placed in a vacuum oven at 120° C. for 90 mins. Each sample was tested to determine its charge density (meq/g), and absorbance/transmittance via Fourier Transform Infrared Spectroscopy (FTIR) at 1720cm⁻¹. The FTIR spectra for the charge-modified pectin and for unmodified pectin is provided in FIG. 4. Charge density values are reported according to the titration method described in Example 1.1. It should be noted that in this example, charge density values of the raw materials are measured and then subtracted from measured values to show a degree of change in charge density above that of the raw biopolymer.

TABLE 22 Process and formulation parameters for preparing charge-modified pectin. Sample # Sample 3.2A Sample 3.2B Temperature (° C.) 140 140 RPM 120 120 Post Treatment No Yes Citric Acid (% relative to pectin) 150 150 SHP (% relative to Citric Acid)  20  20

TABLE 23 Properties of the charged-modified pectin. Sample # FTIR (% Trans.) Titration (meq/g) 3.2A 59.1 4.96 3.2B 26.6 5.72

A charge-modified pectin was produced via reactive extrusion. FTIR analysis shows % Transmission values significantly lower than that of unmodified pectin (63%) and titration values significantly greater than that of unmodified pectin (0 meq/g), indicating charge modification of the pectin.

Example 3.3—Extruded Charge Modified Biopolymer (Demonstration of Charge Grafting onto Soy Protein)

Soy protein was charge modified to form an anionic soy protein using the DSM extruder described in Example 1.1. In preparing the charge-modified soy protein, Experimental methods followed those in Example 3.1. Table 24 sets forth the ranges for the temperature, screw rpm, and amount of citric acid tested using the twin screw conical extruder.

TABLE 24 Parameter ranges for charge-modified soy protein via twin screw conical extruder. Temperature Ranges (° C.) 90-150 RPM Ranges (RPM) 50-200 Citric Acid Ranges (wt % relative 40-150 to soy protein)

Table 25 provides specific parameters tested with test responses described in Table 26. If the sample underwent a post treatment, then the sample was placed in a vacuum oven at 120° C. for 90 mins. Each sample was tested to determine its charge density (meq/g), and absorbance/transmittance via Fourier Transform Infrared Spectroscopy (FTIR) at 1720cm⁻¹. The FTIR spectra for the charge-modified soy protein and for unmodified soy protein is provided in FIG. 5. Charge density values are reported according to the titration method described in Example 1.1. It should be noted that in this example, charge density values of the raw materials are measured and then subtracted from measured values to show a degree of change in charge density above that of the raw biopolymer.

TABLE 25 Process and formulation parameters for preparing charge-modified soy protein. Sample # Sample 3.3A Sample 3.3B Temperature (° C.) 140 140 RPM 120 120 Post Treatment No Yes Citric Acid (wt % relative to 150 150 Hemicellulose) SHP (wt % relative to soy protein)  20  20

TABLE 26 Properties of the charged-modified soy protein. Sample # FTIR (% Trans.) Titration (meq/g) 3.3A 68.4 1.66 3.3B 42.8 4.68

A charge-modified soy protein was produced via reactive extrusion. FTIR analysis shows % Transmission values significantly lower than that of unmodified soy protein (93%) and titration values significantly greater than that of unmodified pectin (0 meq/g), indicating charge modification of the soy protein. Charge modification was enhanced by thermal post treatment.

Example 4.1—Extruded Cross Linked Biopolymer (Demonstration of Starch Modified With a Range of Cross Linkers)

In addition to charge modifiers, cross-linkers were utilized to form a cross-linked starch using the DSM extruder described in Example 1.1. In preparing the cross-linked starch, experimental methods followed those in Example 1.1. The following parameters are varied: temperature, screw rpm, and the amount of cross linker. In this example, water was used as the plasticizer at the level of 40 wt % relative to starch. Cross linkers included: Epichlorohydrin (EPI, >=99% (GC), Item 45340, Sigma-Aldrich, St. Louis, Mo.), Poly(ethylene glycol) diglycidyl ether (PEDGE, Avg. MN 500, Item 475696, Sigma-Aldrich, St. Louis, Mo.), and Poly(propylene glycol) diglycidyl ether (PPDGE, Avg. CA. 640, Item 406740, Sigma-Aldrich, Mo., St. Louis) with sodium hydroxide as catalyst. Table 27 sets forth the ranges for the temperature, screw rpm, and amount of cross-linker tested using the twin screw conical extruder. Table 28 provides specific parameters tested with test responses described in Table 29.

TABLE 27 Process and formulation ranges for preparing cross-linked starch. Temperature (° C.) 80-110 RPM 50-120 Crosslinker Epichlorohydrin, PEDGE, and PPDGE Crosslinker (wt % relative to starch) 0.01-0.1  NaOH (wt % relative to Starch) 0.005-0.2  

TABLE 28 Process and formulation parameters for preparing cross-linked starch. Sample 4.1A Sample 4.1B Sample 4.1C Temperature (° C.) 90 90 90 RPM 120 120 120 Post-treatment No No No Crosslinker EPI PEDGE PPDGE Crosslinker (wt % 0.1 0.1 0.1 relative to starch) NaOH (wt % 0.2 0.2 0.2 relative to Starch) Plasticizer (40% Water Water Water relative to starch)

TABLE 29 Properties of cross-linked starch. Solubility (%) Swelling (g/g) Sample 4.1A 1.6 0.35 Sample 4.1B 2.53 2.67 Sample 4.1C 4.07 3.15

Here, cross-linked biopolymers were produced via a reactive extrusion process. Reactive extrusion of starch with cross linkers show: as cross linker chain length (molecular weight) is increased (EPI<PEDGE<PPDGE), swelling values improve beyond that of uncross-linked starch (0.4g/g) and solubility values approach that of uncross-linked starch (7%).

Example 4.2—Extruded, Cross Linked, Charge Modified Biopolymer (Demonstration of Cationic Starch Modified With Various Cross Linkers)

In addition to starch, charge-modified starch were utilized to form a cross-linked, charge-modified starch using the DSM extruder described in Example 1.1. In preparing the cross-linked, charge-modified starch, experimental methods followed those in Example 4.1. Aquaflocc 330 AW, manufactured by Aquasol Corp (Rock Hill, S.C.) was used as the cationic starch in this example. Additional commercially-available cationic starches, as well as cationic starches as described in Example 2.2 were also utilized. The following parameters are varied: temperature, screw rpm, amount of cross linker, and plasticizer. Cross linkers included: Epichlorohydrin, Poly(ethylene glycol) diglycidyl ether, and Poly(propylene glycol) diglycidyl ether with sodium hydroxide as catalyst. Table 30 sets forth the ranges for the temperature, screw rpm, and amount of cross-linker tested using the twin screw conical extruder. Table 31 provides specific parameters tested with test responses described in Table 32.

TABLE 30 Process and formulation ranges for preparing cross-linked, cationic starch. Temperature (° C.) 80-160 RPM 10-300 Crosslinker (wt % relative to starch) 0.0001 to 10 NaOH (wt % relative to Starch)  0.001 to 20 Plasticizer (%) Water, Glycerol (20-50%)

TABLE 31 Process and formulation parameters for preparing cross-linked, cationic starch. Sample 4.2A Sample 4.2B Sample 4.2C Temperature (° C.) 90 90 90 RPM 120 120 120 Post-treatment No No No Crosslinker EPI PEDGE PPDGE Crosslinker (wt % 0.1 0.1 0.1 relative to starch) NaOH (wt % 0.2 0.2 0.2 relative to Starch) Plasticizer (% Water Water Water relative to starch) (40%) (40%) (40%)

TABLE 32 Properties of cross-linked cationic starch. Solubility (%) Swelling (g/g) Sample 4.2A 12.6 1.9 Sample 4.2B 39.9 11.2 Sample 4.2C 40.3 14.7

Here, cross linked, charge modified biopolymers were created via reactive extrusion. Solubility results show values significantly lower than that of the raw material (84%). Here, decreasing solubility indicates increased degree of cross-linking. Swelling results may be higher or lower than that of the raw material (4.4 g/g) depending on degree of cross-linking.

Example 5.1—Extruded Cross Linked, Charge Modified Biopolymer (Demonstration of Cross Linking Multiple Biopolymers Using 2-Step, in Line Method)

To demonstrate crosslinking two charge modified biopolymers, cross-linked, charged-modified starch citrate chitosan was prepared using a 2-step inline process using the Leistritz, 18 mm extruder as described in Example 1.1. Grafting citric acid onto starch provides an anionic charge, which changes the degree of charge as can be measured using back titration (meq/g). Acetic acid may be used to protonate chitosan upon mixing, thereby providing a cationic charge on the chitosan. The charge-modified chitosan may be assumed to be partially (i.e., 50% or more) or fully (100%) protonated due to its solubility in water.

Furthermore, the extruder having multiple zones as shown in FIG. 2, allows for implementation of temperature and injection profiles. Extrusion and composition parameters for preparing cross-linked, charge-modified starch citrate chitosan were varied as described in Table 33. Here, powder samples of starch, citric acid, and SHP were fed into the initial injection zone (Step 1), while chitosan (Trading Resources, Cocoa Beach, Fla.), acetic acid (Sigma Aldrich, Item # A6283, St. Louis, Mo.), and plasticizers were simultaneously added in at injection zone 3 (Step 2) as shown in Table 34 below. Reactions zones 1-2 were used for charge modification, while reaction zones 3-8 were used for crosslinking the charge modified-starch to charge-modified chitosan. Temperature profiles for each zone are provided in Table 34 below. Screw profile utilized largely conforms to the medium shear screw as described in FIG. 6 (medium shear screw). After the graft reaction of citric acid onto starch, the temperature was decreased to 100° C. to allow for the injection of protonated chitosan inside the extruder in zone 3 before raising the temperature to 105° C. and 110° C. in zones 4 and 5, respectively, to initiate the crosslinking reaction between the starch carboxylate and the free amine groups on the backbone of chitosan. In some runs, extruded samples in solid form were post-treated by placing the charge-modified, cross-linked polymer in an oven at 120° C. for 90 minutes. The simultaneous injection of two mixtures demonstrated below is defined as a 2-step, inline reaction.

TABLE 33 Parameter ranges for cross-linked starch citrate chitosan via parallel twin screw extruder. Temperature Ranges (° C.) 100-120 (see Table 34) RPM Ranges (RPM) 140-170 Chitosan Ranges (wt % relative to Starch) 100 Acetic Acid Ranges (wt % relative to Chitosan)  33 Starch Citrate Ranges (wt % relative to Chitosan) 100 Plasticizer Types Citric Acid Plasticizer Ranges (wt % relative to Chitosan)  90-140

TABLE 34 Example of temperature and injection profile for charge-modified starch cross- linked to another biopolymer via parallel twin-screw extruder. Zone 1 2 3 4 5 6 7 8 Temperature (° C.) 120 120 100 105 110 110 110 105 Injection Starch + N/A N/A Chitosan + N/A N/A N/A N/A N/A Reagents Reagents

Specific examples of process parameters and resulting responses are shown in Tables 35 and 36 below, respectively. The methods for determining the measured responses (e.g. solubility, DI uptake, and extractables) are described in Example 1. For FTIR analysis, bonds of interest for charged-modified starch, cross linked to chitosan system include the Amide-Carbonyl (R—CO—CNH—R) stretch at ˜1650 cm⁻¹.

TABLE 35 Process parameters for preparing cross-linked, charge-modified starch citrate chitosan. Sample # Sample 5.1A Sample 5.1B Sample 5.1C Temperature (° C.) 100-120 100-120 100-120 (multiple (multiple (multiple zones) zones) zones) RPM 140  140  170  Post Treatment Yes No Yes Reaction Type 2-step inline 2-step inline 2-step inline Plasticizer Type Citric Acid Citric Acid Citric Acid Plasticizer (wt % 75 75 75 relative to Chitosan) Starch Citrate (wt % 100  100  100  relative to Chitosan) Acetic Acid (wt % 33 33 33 relative to Chitosan)

TABLE 36 Properties of the cross-linked, charge- modified starch citrate chitosan. Solubility FTIR DI Uptake Extractables Sample # (%) (% Trans) (g/g) (%) 5.1A 4.1 67.5 2.6 19 5.1B 2.4 65.4 9.5 69 5.1C 4.1 68.2 1.9 19

As described in Example 2, charge modified polymers without cross-linking show increasing solubility with increasing charge density (>5% and up to 100%). Due to the presence of charge modified starch and charge modified chitosan, solubility values <5% indicate presence of crosslinking. FTIR analysis confirms presence of the amide-carbonyl stretch where a modified and unmodified chitosan shows transmission values of 26% and modified and unmodified starch shows values of 5%. % Transmission values above 26% indicate presence of charge modified starch cross linked to charge modified chitosan, confirming the ability to form a charge modified biopolymer cross linked to another biopolymer in a 2-step, in-line method.

Example 5.2—Extruded Cross Linked, Charge Modified Biopolymer (Demonstration of Cross Linking Multiple Biopolymers Using 2-step, 2-Pass Method)

To demonstrate a method where charged-modified biopolymers may be produced and subsequently cross linked to another biopolymer, charged-modified starches as prepared in Example 1.1 were cross-linked with chitosan by mixing powdered starch citrate (i.e., the citric acid-modified starch) with acetic acid, chitosan, and plasticizer so that the mixture was in powdered form. To obtain the powdered charge-modified starch, the charge-modified starch was ground using a blender to sugar/starch consistency where there were no visible chunks/inconsistencies in the powder mixtures. At least one plasticizer selected from: glycerol [Item #0854, Amresco, Solon, Ohio], citric acid, and polyethylene glycol [molecular weights of 400, 800, 20,000, Sigma Aldrich, St. Louis, Mo.] was added to the mixture comprising of starch citrate, acetic acid, chitosan, and plasticizer to induce melt blending during the extrusion process. The resulting powder mixture was added to the extruder described in Example 1.1 in a method resembling the process for preparing charge-modified starch as described in Example 1.1. Extrusion parameters and compositions were modified according to Table 37 below.

TABLE 37 Parameter ranges for cross-linked, charge-modified starch citrate chitosan via twin screw conical extruder. Temperature Ranges (° C.) 90-130 RPM Ranges (RPM) 60-200 Chitosan Ranges (rel % to Starch) 50-150 Acetic Acid Ranges (rel % to Chitosan)  5-100 Starch Citrate Ranges (rel % to Chitosan) 150-250  Plasticizer Types Glycerol Citric Acid, Water Plasticizer Ranges (rel % to Chitosan) 120-275 

Completion of the reaction in two steps is defined here as a “2-step, 2-pass” reaction. Examples of process parameters for cross-linked, charge-modified starch citrate chitosan and measured responses are shown in Tables 38 and 39, respectively below. The charge-modified starch used to prepare the cross-linked, charge-modified starch citrate chitosan had previously been prepared as described in Example 1 according to parameters described in sample 1.1A.

Each sample was analyzed via FTIR to characterize chemical identity, determine its deionized water (DI) uptake, and to measure extractables (inverse of yield) following the methods described in Example 1.

TABLE 38 Process parameters for preparing cross-linked, charge-modified starch citrate chitosan. Sample # Sample 5.2A Sample 5.2B Extruder DSM DSM Temperature (° C.) 100 110 RPM 120 120 Post Treatment No No Reaction Type 2-step, 2-pass 2-step, 2-pass Plasticizer Type Citric acid Citric Acid Plasticizer (wt % 175 175 relative to Chitosan) Starch Citrate (wt % 100 250 relative to Chitosan) Acetic Acid (wt % 33 33 relative to Chitosan)

TABLE 39 Properties of the cross-linked starch citrate chitosan. FTIR DI Uptake Extractables Sample # (% Trans) (g/g) (%) 5.2A 59.4 2.7 73 5.2B 62.6 1.5 61

As described in Example 5.1, a citric acid modified starch cross-linked to chitosan may show the amide-carbonyl (R—CO—CNH—R) stretch at ˜1650 cm⁻¹ when subjected to FTIR analysis. FTIR analysis confirms presence of the amide-carbonyl stretch where a modified and unmodified chitosan shows transmission values of 26% and modified and unmodified starch shows values of 5%. Here, % Transmission values of 59 and 62% (>26%) indicate presence of charge modified starch cross linked to charge modified chitosan and confirming the ability to form a charge modified biopolymer cross linked to another biopolymer in a 2-step, 2-pass method.

Example 5.3—Extruded Cross Linked, Charge Modified Biopolymer (Demonstration of Cross Linking Multiple Biopolymers Using All-In-One Method)

To demonstrate simultaneous charge modification and cross-linking via reactive extrusion, all raw materials (i.e., starch, citric acid, SHP, chitosan, acetic acid, and plasticizer as described in Examples 5.1 and 5.2) were injected simultaneously in powder form to induce charge modification and cross-linking reactions in one injection through multiple extruders (defined here as an “all-in-one” reaction). Here, the mixture of all raw materials was added to the extruder described in Example 1.1 and 1.3 in a method resembling the process for preparing charge-modified starch as described in Example 1.1 and 1.3. Extrusion parameters and compositions were modified according to Table 40 below. Examples of process parameters for preparing cross-linked, charge-modified starch citrate chitosan are shown in Table 41 below with measured responses provided in Table 42. The methods for determining the measured responses are provided in Examples 1 and 2.

TABLE 40 Parameter ranges for cross-linked, charge-modified starch citrate chitosan via twin screw conical extruder and 52 mm. parallel twin screw extruder. Extruder DSM Wegner TX-52 Temperature Ranges (° C.) 90-130 105-130 RPM Ranges (RPM) 60-200 120-250 Chitosan Ranges (wt % 50-150 50-75 relative to Starch) Acetic Acid Ranges (wt %  5-100 N/A relative to Chitosan) Starch Ranges (wt % 150-250  100 relative to Chitosan) Plasticizer Types Glycerol Citric Citric Acid, Acid, Poly Ethylene Water Glycol, Water Plasticizer Ranges (wt % 120-275  100-130 relative to Chitosan)

TABLE 41 Process parameters for preparing cross-linked, charge-modified starch citrate chitosan. Sample # Sample 5.3A Sample 5.3B Sample 5.3C Sample 5.3D Extruder DSM DSM Wegner Wegner TX-52 TX-52 Temperature 100 133 120 110 (° C.) RPM 120 120 120 200 Post Treatment No No No No Reaction Type All- All- All- All- in-one in-one in-one in-one Plasticizer Citric Glycerol Citric Citric Type Acid Acid Acid Plasticizer (% 175 175 100 100 rel to Chitosan) Starch (% rel 150 100 150 150 to Chitosan) Citric Acid (% 66 66 N/A N/A rel to Starch) SHP (% rel to 20 20  20  20 Starch) Acetic Acid (% 33 33 N/A N.A rel to Chitosan)

TABLE 42 Properties of the cross-linked, charge- modified starch citrate chitosan. FTIR DI Uptake Extractables Sample # (% Trans) (g/g) (%) 5.3A 58.8 4.3 58 5.3B 66.9 4.9 54 5.3C 67.2 N/A 67 5.3D 65.3 N/A 65

As described in Example 5.1 and 5.2, a citric acid modified starch cross-linked to chitosan may show the Amide-Carbonyl (R—CO—CNH—R) stretch at ˜1650 cm⁻¹ when subjected to FTIR analysis. The presence of carbonyl groups indicate citric acid charge modification on starch, and the presence of the Amide-carbonyl group indicates cross-linking. FTIR analysis confirms presence of the Amide-carbonyl stretch where a modified and unmodified chitosan shows transmission values of 26% and modified and unmodified starch shows values of 5%. Here, % Transmission values of >26% indicate simultaneous charge modification and cross linking of charge modified starch cross linked to chitosan to form a charge modified biopolymer cross linked to another biopolymer in an all-in-one method.

Example 6—Example of Modified Biopolymer for IEX Application (Demonstration of Salt/Heavy Metal Uptake)

To demonstrate ion removal capabilities of a charge modified, cross linked biopolymer, citric acid-modified starch cross-linked to chitosan were prepared according to Examples 5.1, 5.2, and 5.3. Samples were tested for their salt uptake capacity measured by conductivity and ash content post exposure to a saline solution.

Ash content testing is a measure of residual inorganic material in a sample upon exposure to high temperatures. 0.3 g of samples was exposed to a 10% saline (NaCl) solution for 5 minutes, then squeezed by hand to remove absorbed liquids. Samples were then transferred to clean, dry, glass vials whose weights were previously recorded. Samples were then exposed to high temperatures in a muffle furnace (Vulcan, Model 3-550), for 4 hours at 575° C. following TAPPI Standard: T211 om-02—“Ash in wood, pulp, paper and paperboard, combustion at 525° C.”. To determine the ash content, the vial weight was subtracted from the final recorded weight comprising of vial and ash. Final ash weight was assumed to be residual captured salts where the final ash weight is divided by the initial sample weight to normalize data to a g NaCl/g sample (g/g) format.

Conductivity is a measure of ionic mobility in a given solution. Reductions in conductivity may be attributed to captured ions, changes in system energy (i.e., temperature, pressure, etc.), and/or potential of dissolved ions (i.e., pH changes in presence of acids/bases). Samples (0.3 g) were exposed to 25 ml of 10% NaCl solution where initial conductivity (Metler-Toledo conductivity instrument [model #51302530]) was measured to be 142 mS/cm with a standard deviation of 3.7. Final conductivity measurements were assumed to be attributed to ion capture and was therefore used to calculate a percent difference in conductivity (captured salt). The uptake of salt was correlated to the resulting decrease in conductivity by the following formula:

Uptake=(volume in mL*salinity* % Δ)/sample weight,

where % Δ is the % change in conductivity. The % change in conductivity is attributed to a reduction in mass of NaCl in solution and is normalized to samples weight. The resulting measurement parameter yields salt uptake as g NaCl/g sample.

TABLE 43 Salt removal properties of a charge modified and cross linked biopolymer system. Salt Uptake - Salt Uptake - Sample # Conductivity (g/g) Ash Content (g/g) 5.1A 0.24 0.98 5.1B 0.22 1.1  5.1C 0.16 0.69 5.2A 0.13 N/A 5.2B 0.13 N/A 5.3A N/A 0.1  5.3B 0.25 0.74 5.3C 0.2  N/A 5.3D 0.24 N/A

Here, salt uptake results of a cross linked biopolymer (cross-linked cationic starch as prepared via the method found in Example 4.2) as measured by conductivity show values of 0 g/g. While not wishing to be bound to any particular theory, the presence of amphoteric charge (including both cationic and anionic charge simultaneously) is expected to improve the polymer's interaction with free ions in solution and is shown in Table 43. Data demonstrated the ability of charge modified and cross linked biopolymers to remove ions from solution at a greater rate than a cross-linked biopolymer. Salt uptake is further demonstrated through ash content measurements as shown in Table 43 above.

Example 7—Example of Modified Biopolymer for SAP Application (Demonstration of Charge Modified Starch (Cationic) Crosslinked to Form Superabsorbent

A superabsorbent polymer was prepared using a commercially available charged cationic starch (AquaFlocc 330AW) and a catalyst on the P11 extruder described in Example 1.1. The extruder having multiple zones similar to that shown in FIG. 2, allows for implementation of temperature and injection profiles. Screw profile utilized is described in FIG. 6 (medium shear screw). Extrusion and composition parameters for preparing a material for super absorbent material were varied as described in Table 44. In preparing the super absorbent polymer, powder cationic starch (Aquafloc 330AW) and sodium hydroxide were fed into the initial injection zone via volumetric powder feeder (olumetric MiniTwin Process 11, Typ 567-7660, Thermo Electron/Thermo Fisher Scientific, Germany), while plasticizer (glycerol) was simultaneously added in at injection zone 2 via liquid injector and peristaltic pump (Masterflex P/S Peristaltic Pump, Model No 1300-3600-0004, Thermo Fisher Scientific, USA) with corresponding peristaltic pump head (Masterflex P/S Easy Load II, Model No 955-0000, Thermo Fisher Scientific, USA). In some runs, extruded samples in solid form were post-treated by placing the modified cationic polymer in an oven at 120° C. for 90 minutes. The simultaneous injection of two mixtures demonstrated below is defined as a 2-step, inline reaction.

In preparing the absorbent polymers, the following parameters were varied: temperature, screw rpm, plasticizer, plasticizer concentration, and amount of catalyst. Table 44 sets forth the ranges for the temperature, screw rpm, and amount of catalyst tested using the 11 mm, parallel twin screw extruder.

Samples were tested as absorbents using the EDANA/INDA method WSP 240.2.R3: free swell capacity in saline by gravimetric determination in order to measure the fluid uptake of samples. For the gravimetric method, 0.2 g of sample was sealed in a 2″×2″ teabag. The teabag/sample packet was submerged in a solution for 1 hr, then hanged to dry for 10 mins. Solutions were prepared according to an industrially relevant application (0.9% NaCl). Weight measurements were recorded pre- and-post submerging and normalized for a teabag control sample undergoing the same conditions. The calculation was as follows:

$\frac{W_{w} - W_{b} - W_{i}}{W_{i}}$

where W_(w) is the wet weight of the teabag/sample, W_(b) is the wet weight of the teabag alone, and W_(i) is the initial weight of the teabag/sample.

TABLE 44 Parameter ranges absorbent polymers via twin screw conical extruder. Temperature Ranges (° C.) 80-160 RPM Ranges (RPM) 50-200 Plasticizer Water, Glycerol, PEG Plasticizer (wt % relative to cat. Starch)  20-60% NaOH (wt % relative to cat. starch)  0-30%

Table 45 provides specific parameters tested with specific temperature profiles shown in Table 46 and test responses described in Table 47. Each sample was tested to determine its swelling capacity according to the method described above, and solubility according to the method in example 2.

TABLE 45 Process and formulation parameters for absorbent polymers. Sample # Sample 7A Sample 7B Temperature (° C.) Temp Profile 7 Temp Profile 7 RPM 150 80 Post Treatment Yes Yes Plasticizer (wt % Glycerol (25%) Glycerol (25%) relative to cat. starch) NaOH (wt % relative 7.5% 7.5% to cat. starch)

TABLE 46 Temperature and injection profiles for examples 7A and 7 B: charge-modified starch via 11 mm, parallel twin-screw extruder. Sample # Zone 1 2 3 4 5 6 7 8 Die Temp Profile 7 Unheated 70 75 80 95 110 100 100 100 (° C.) Injection Cat. Starch + Glycerol N/A N/A N/A N/A N/A N/A N/A NaOH 7A Feed Rate 50 5.9 N/A N/A N/A N/A N/A N/A N/A (RPM) 7B Feed Rate 25 2.4 N/A N/A N/A N/A N/A N/A N/A (RPM)

TABLE 47 Properties of the absorbent polymers. Sample # Free Swell Capacity (g/g) Solubility (g/g) 7A 31.6 4.5 7B 28.8 2.0

As shown by results in Table 47, reactive extrusion is used to make a biopolymer material that is useful for absorbing liquids in industrially relevant applications.

Example 8—Example of modified biopolymer for biosorbent application

Additionally, samples as described in Example 7 were tested as absorbents for other fluids using a modified the EDANA/INDA method WSP 240.2.R3: free swell capacity in saline by gravimetric determination in order to measure the fluid uptake of samples. Here, alternative solutions are used as shown in Table 48, in place of the specified 0.9% NaCl (saline). Instant Ocean Seal Salt was used as a sea water simulant. Canola oil, conventional motor oil, and synthetic motor oil, were used as oil references. Gasoline and diesel fuel were used as fuel references, and whole bovine blood was used as a blood reference. The results demonstrated an improved performance for cross-linked, charge-modified biopolymers of the present invention relative to conventional superabsorbent materials: Sodium Polyacrylate (NaPoly, Item 432784, Sigma-Aldrich, St. Louis, Mo.) in Table 48 below.

TABLE 48 Biosorbent properties of a cross-linked, charge-modified biopolymer of the present invention (“Modified Biopolymer”) relative to commercially available superabsorbent polymers (NaPoly). Solution Sample Uptake (g/g) Instant Ocean (Sea Water) Modified Biopolymer 29 Na Poly 19 Canola Oil Modified Biopolymer 18 Na Poly 2.2 Motor Oil (Conventional) Modified Biopolymer 5.3 Na Poly 1.7 Motor Oil (Synthetic) Modified Biopolymer 9.2 Na Poly 2.3 Gasoline Modified Biopolymer 3.9 Na Poly 0.8 Diesel Modified Biopolymer 4.7 Na Poly 3.4 Blood Modified Biopolymer 16.6 Na Poly 1.48

As shown by results in Table 48, reactive extrusion is used to make a biopolymer material that is useful for absorbing liquids in a range of industrially relevant applications.

Example 9—Example of Modified Biopolymer Showing Comparative Homogeneity (Homogeneity Analysis)

A JEOL JSM-6010LA scanning electron microscopy (SEM) with a solid state EDS detector was used to characterize and compare samples. Samples were adhered to a mount using double sided carbon tape and analyzed at 20 kV. Micrographs were collected along with corresponding EDS scans of the target area.

Indications of homogeneity were derived from the comparison of commercially available cationic starch to an extruded cationic starch of the present invention (Example 2.2C). AquaFlocc 330AW manufactured by Aquasol Corp (Rock Hill, S.C.) represented the commercially available starch. It is believed that the commercially available cationic starch is modified in a dry process, which maintains starch in granular form and allows only for surface modification of the starch. In contrast, while not wishing to be bound to any particular theory, the extrusion process is believed to completely destroy the granular structure of the biopolymer (e.g., starch).

As can be seen in FIGS. 7A and 7B, which are SEM images of commercially available starch, the commercially available starch retains the starch's characteristic granular structure. In contrast, as can be seen in FIGS. 7D and 7E, which are SEM images of extruded cationic starch prepared according to methods of the present invention, starches extruded according to embodiments of the present invention exhibit complete destruction of the granular structure and morphology arises only from topology in sample preparation. This can be seen by comparing FIGS. 7A and 7B with FIGS. 7D and 7E.

Furthermore, when exposed to water and dried, the commercially available starches showed the presence of insoluble materials. These insoluble materials indicate uncharged or lowly charged regions, which are a product of inhomogeneous processing. These results were confirmed via Energy-Dispersive X-ray Spectroscopy (EDS of EDXS), which was used to map the elemental composition of the SEM image for the commercially available starch (FIG. 7C) and the extruded cationic starch prepared according to methods of the present invention (FIG. 7F). As can be seen in FIG. 7C, a clear/defined dark region is present where the discrete particles are imaged. This indicates that these particles are different in composition (lacking chlorine) compared to the surrounding region. In contrast, as can be seen in FIG. 7F, EDS scans of the extruded starch show a gradual change in contrast towards the bottom right of the image. This change correlates to a sloping region on the SEM image towards the bottom right. However, the top left of the image in FIG. 7F also shows a sloping region in the SEM image, with little change in the EDS map. Thus, it can be concluded that any contrast here is from a shadowing effect, rather than a compositional effect and the sample is therefore homogeneous.

The foregoing is illustrative of the present invention, and is not to be construed as limiting thereof. The invention is defined by the following claims, with equivalents of the claims to be included therein. All publications, patent applications, patents, patent publications, and other references cited herein are incorporated by reference in their entireties for the teachings relevant to the sentence and/or paragraph in which the reference is presented. 

We claim:
 1. A method for producing a cross-linked, charge-modified biopolymer comprising: combining a biopolymer and a plasticizer to form a homogenous reaction blend, wherein the homogenous reaction blend comprises a plasticized biopolymer; reacting the plasticized biopolymer and at least one charge-modifying agent in the homogenous reaction blend to form a charge-modified biopolymer; and cross-linking the charge-modified biopolymer to form a cross-linked, charge-modified biopolymer, wherein the cross-linked, charge modified starch is free of crystalline domains.
 2. The method of claim 1, wherein the combining step further comprises combining a catalyst with the biopolymer and the plasticizer to form the homogenous reaction blend.
 3. The method of claim 1, wherein the cross-linking step further comprises reacting the charge-modified biopolymer with at least one cross-linking agent.
 4. The method of claim 1, wherein the biopolymer comprises at least two different biopolymers.
 5. The method of claim 1, wherein the cross-linked, charge-modified biopolymer has a net positive charge.
 6. The method of claim 1, wherein the combining step comprises melt blending the biopolymer and the plasticizer using a reactive extrusion process.
 7. The method of claim 1, wherein the method is carried out in an extruder.
 8. The method of claim 1, wherein the cross-linked, charge-modified biopolymer is in the form of a particle have a diameter in a range of about 10 microns to about 1000 microns.
 9. The method of claim 1, wherein the reacting and/or cross-linking step(s) is/are carried out at a temperature in a range of about 80° C. to about 150° C.
 10. The method of claim 1, further comprising heating the cross-linked, charge-modified biopolymer at a temperature in a range of about 100° C. to about 150° C. for a period of time in a range of about 1 minute to about 8 hours.
 11. The method of claim 1, wherein the cross-linked, charge-modified biopolymer has a net negative charge.
 12. The method of claim 11, wherein the cross-linked, charge-modified biopolymer includes at least one negatively charged moiety selected from the group consisting of a carboxyl, sulfonate, a sulfate, and phosphate.
 13. A cross-linked, charge-modified biopolymer prepared according to the method of claim
 1. 14. The cross-linked, charge-modified biopolymer of claim 13 having a charge density of at least 3 meq/g as determined by titration.
 15. A cross-linked, charge-modified biopolymer, wherein the cross-linked, charge- modified biopolymer is cationic, wherein the cross-linked, charge-modified biopolymer is free of crystalline domains, and wherein the biopolymer is starch.
 16. The cross-linked, charge-modified biopolymer of claim 15, wherein the cross-linked, charge-modified biopolymer has a degree of substitution of at least 0.1, as measured by nitrogen content.
 17. The cross-linked, charge-modified biopolymer of claim 15, wherein the cross-linked, charge-modified biopolymer includes at least one positively charged moiety selected from the group consisting of a quaternary ammonium, sulfonium, and/or phosphonium group.
 18. A cross-linked, charge modified biopolymer, wherein the cross-linked, charge modified biopolymer is anionic and wherein the cross-linked, charge modified biopolymer is free of crystalline domains, and wherein the biopolymer is starch.
 19. The cross-linked, charge-modified biopolymer of claim 18, wherein the cross-linked, charge modified biopolymer has a degree of substitution of at least 0.1, as measured by nitrogen content.
 20. The cross-linked, charge-modified biopolymer of claim 18, wherein the cross-linked, charge-modified biopolymer includes at least one negatively charged moiety selected from the group consisting of a carboxyl, sulfonate, a sulfate, and phosphate. 